飞秒激光作用下的硅表面微结构及发光特性 被引量:18

Microstructure and fluorescence property of silicon fabricated by femtosecond laser
下载PDF
导出
摘要 采用近红外飞秒激光辐照浸泡在硫酸溶液中的N型单晶硅片,激光波长800nm。脉宽200fs。重频1kHz,平均功率为100mw,而硫酸溶液的质量分数分别选择为0.1%和1%。辐照后硅表面呈直径为5~8pm,高度15pm的柱型结构。分析其荧光特性,并通过比较硅材料表面微结构与激光光源、扫描参数、硅片背景环境的关系,确定最佳辐照条件为激光扫描速度750pm/s,扫描间距5m/s。最终在厚度0.5mm、直径26mm的硅片上获得10mm×10mm的方形扫描区域,荧光光谱显示激光扫描后的区域在700nm附近有很强的荧光发射。分析结果表明飞秒激光扫描改变了样品的表面微结构尺寸,增大了吸收面积,扩展了荧光激发波长,有效提高了样品的吸收效率和荧光发光相对强度(超过扫描前发光相对强度的2倍),荧光发射谱的变化是由量子限制效应和表面态模型共同作用的结果。 The micro-structure surface and fluorescence of silicon slice fabricated by femtosecond laser under the assistant of low consistency sulfuric acid liquor are reported. A 10 mm× 10 mm square region was fabricated from 0.5 mm thick and 26 mm in diameter silicon slice. The absorbency is increased due to the change of the surface microstructure of the silicon. Photoluminescence spectra display a high fluorescence emission at the wavelength from 700 nm to 750 nm, thus show a new and simple method to increase the fluorescence property of silicon.
出处 《强激光与粒子束》 EI CAS CSCD 北大核心 2006年第7期1081-1084,共4页 High Power Laser and Particle Beams
关键词 单晶硅 飞秒激光 微结构 荧光特性 Crystalline silicon Femtosecond laser Micro-structure Fluorescence property
  • 相关文献

参考文献18

  • 1Cheng G H,Wang Y S,White J D,et al.Demonstration of three-dimensional storage in fused silica with femtosecond laser pulses[J].Journal of Applied Physics,2003,94:1283.
  • 2杨建军.飞秒激光超精细“冷”加工技术及其应用(I)[J].激光与光电子学进展,2004,41(3):42-52. 被引量:42
  • 3程光华,王屹山,刘青,赵卫,陈国夫.用飞秒激光脉冲在PMMA内页面式写入三维光存储的研究[J].物理学报,2004,53(2):436-440. 被引量:8
  • 4Amoruso S,Ausanio G,Bruzzese R,et al.Femtosecond laser pulse irradiation of solid targets as a general route to nanoparticle formation in a vacuum[J].Physical Review B,2005,71:033406.
  • 5Colombier J P,Combis P,Bonneau F,et al.Hydrodynamic simulations of metal ablation by femtosecond laser irradiation[J].Physical Review B,2005,71:165406.
  • 6Jia T Q,Chen H X,Huang M,et al.Formation of nanogratings on the surface of a ZnSe crystal irradiated by femtosecond laser pulses[J].Physical Review B,2005,72:125429.
  • 7Vorobyev A Y,Chunlei G.Enhanced absorptance of gold following multipulse femtosecond laser ablation[J].Physical Review B,2005,72:195422.
  • 8曹小龙,李清山,张淑芳.硅纳米颗粒和多孔硅的荧光光谱研究[J].光电子.激光,2004,15(9):1113-1117. 被引量:5
  • 9张占军,李经建,张波,蔡生民.多孔硅表面性质导致电致发光的进一步论证[J].电化学,2002,8(1):9-14. 被引量:4
  • 10Wu C,Crouch C H,Zhao L,et al.Visible luminescence from silicon surfaces micro-structured in air[J].Applied Physics Letters,2002,81(11):1999-2001.

二级参考文献28

  • 1陈开盛.亚微米光刻与光掩模新技术现状与研发前景[J].半导体技术,2000,25:18-21.
  • 2傅金泉.中国红曲及实用技术[M].北京:中国轻工业出版社,1997..
  • 3魏景超.真菌鉴定手册[M].上海:上海科学出版社,1997..
  • 4Canham L T.Silicon quantum wire array fabrication by electrochemical and chemical dissolution of wafers[J].Appl Phys Lett,1990,57:1046-1048.
  • 5Belomoin Gennadiy,Therrien Joel,Nayfeh Munir.Oxide and hydrogen capped ultrasmall blue luminescent Si nanoparticles[J].Appl Phys Lett,2000,77:779-781.
  • 6Rubanyi G M.The future of human gene therapy[J].Mol Aspects Med,2001,22(3):113-142.
  • 7Den Luo,Mark S.Enhancement of transfection by physical concentration of DNA at the cell surface[J].Nat Biot,2000,13:893-895.
  • 8Carsten K,Mohammad S,Elenore G.Silica nanoparticle modified with aminosilanes as carriers for plasmid DNA[J].Intern J of Pharmac,2000,196:257-261.
  • 9Truong Le V L, Walsh S M, Schweibert E, et al.Genetransfer by DNA-gelatin nanospheres[J].Arch of Biochemand and Bioph,1990,361:47-56.
  • 10Liu Xingna,Wu Xiaowei,Bao Ximao,et al.Photoluminescence from nanocrystallities embedded in hydrogenated amorphous silicon films prepared by plasma enhanced chemical vapor deposition[J].Appl Phys Lett,1994,64:220-222.

共引文献56

同被引文献273

引证文献18

二级引证文献68

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部