摘要
Photostimulated luminescence was observed in X-ray irradiated BaBrCl doped with Eu^2 ＋ . It shows an emission band that peak at 413 nm, and two difference absorption spectra （DAS） bands that peak at - 550 nm and 675 nm respectively. The stimulation energy is lower than that of BaFX：Eu^2＋ （X = Cl, Br）, and matches the cheaper, more portable, and more convenient semiconductor laser better. The results indicate that BaBrCl ： Eu^2＋ shows positive potential as a promising X-ray storage phosphor for practical utilization.
Photostimulated luminescence was observed in X-ray irradiated BaBrCl doped with Eu^2 ＋ . It shows an emission band that peak at 413 nm, and two difference absorption spectra （DAS） bands that peak at - 550 nm and 675 nm respectively. The stimulation energy is lower than that of BaFX：Eu^2＋ （X = Cl, Br）, and matches the cheaper, more portable, and more convenient semiconductor laser better. The results indicate that BaBrCl ： Eu^2＋ shows positive potential as a promising X-ray storage phosphor for practical utilization.
基金
Project supported bythe National Natural Science Foundation of China (10274001)
the Teaching and Research Award Pro-gramfor Outstanding Young Teachersin Higher EducationInstitutions of MOE,P.R.C.(TRAPOYT) ,Cross-Century Educa-tion Plan for Good Talent ,and Innovation Project of Beijing Jiaotong University (48002)