Effect of Aging Temperature on Erosion-Corrosion Behavior of 17-4PH Stainless Steels in Dilute Sulphuric Acid Slurry 被引量:18

Effect of Aging Temperature on Erosion-Corrosion Behavior of 17-4PH Stainless Steels in Dilute Sulphuric Acid Slurry
下载PDF
导出
摘要 The effect of aging temperature on erosion corrosion (E-C) behavior of 17-4PH stainless steels in dilute sulphuric acid slurry containing solid particles was studied by using self-made rotating E-C apparatus. The effect of impact velocity on EC behavior of 17 4PH steels at different aging temperatures was analyzed. Surface micrographs of the specimens after E C test were observed by using scanning electron microscope (SEM). The results showed that under the condition of the same solution heat treatment, when aging temperature ranged from 400 ℃ to 610℃, the hardness reached the highest value near the temperature 460℃. The characteristics of E-C for 17-4PH stainless steels at different aging temperatures were as follows: pure erosion (wear) was dominant, corrosion was subordinate and at the same time corrosion promoted erosion. The effect of aging temperature on E-C rate of 17-4PH steels was not significant at low impact velocity, but it was found that E-C resistance of 17-4PH steels aged near 460℃ was the most excellent due to the best precipitation strengthening effect of fine and dispersed e-Cu phase. With a prerequisite of appropriate corrosion resistance, the precipitation hardening could significantly improve the E-C resistance of the materials. The effect of aging temperature on erosion corrosion (E-C) behavior of 17-4PH stainless steels in dilute sulphuric acid slurry containing solid particles was studied by using self-made rotating E-C apparatus. The effect of impact velocity on EC behavior of 17 4PH steels at different aging temperatures was analyzed. Surface micrographs of the specimens after E C test were observed by using scanning electron microscope (SEM). The results showed that under the condition of the same solution heat treatment, when aging temperature ranged from 400 ℃ to 610℃, the hardness reached the highest value near the temperature 460℃. The characteristics of E-C for 17-4PH stainless steels at different aging temperatures were as follows: pure erosion (wear) was dominant, corrosion was subordinate and at the same time corrosion promoted erosion. The effect of aging temperature on E-C rate of 17-4PH steels was not significant at low impact velocity, but it was found that E-C resistance of 17-4PH steels aged near 460℃ was the most excellent due to the best precipitation strengthening effect of fine and dispersed e-Cu phase. With a prerequisite of appropriate corrosion resistance, the precipitation hardening could significantly improve the E-C resistance of the materials.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2006年第5期73-78,共6页
关键词 aging temperature 17-4PH precipitation-hardened stainless steel erosion-corrosion (E-C) HARDNESS aging temperature 17-4PH precipitation-hardened stainless steel erosion-corrosion (E-C) hardness
  • 相关文献

同被引文献133

引证文献18

二级引证文献166

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部