摘要
采用Moldflow公司MPI软件中的Co-injection分析模块,对夹芯注射成型过程进行动态模拟分析；揭示不同材料种类组合对夹芯注射成型过程中残余应力的影响规律。结果发现,夹芯注射体系中两种物料相容性的好坏对芯/壳层界面处残余应力的分布有较大影响,芯层为结晶型材料时会导致残余应力有较大的跃迁。
In order to understand the mechanism in the sandwich injection molding, a dynamic simula- tion was carried out employing a co-injection module in the software of Moldflow. It was found that the compatibility of two materials determined the residual stress distribution at the interface of core/skin melts. When the core melt was crystallizable, greater residual stress transition may occur.
出处
《中国塑料》
CAS
CSCD
北大核心
2006年第9期45-48,共4页
China Plastics