Due to its mechanical properties and ease of use, vinyl ester resin is enjoying increasing consideration. This resin normally is produced by reaction between epoxy resin and unsaturated carboxylic acid. In the present study, bis-phenol A based epoxy resin and methacrylic acid was used to produce vinyl ester resin. The reaction was conducted under both stoichiometric and non-stoichiometric conditions in the presence of triphenylphosphine as catalyst. The stoichiometric and non-stoichiometric experiments were conducted at 95, 100, 105 and 110℃and at 90 and 95℃, respectively. The first order rate equation and mechanism based rate equation were examined. Parameters are evaluated by least square method. A comparison of mechanism based rate equation and experimental data show an excellent agreement. Finally, Arrhenius equation and activation energy were presented.
Due to its mechanical properties and ease of use, vinyl ester resin is enjoying increasing consideration. This resin normally is produced by reaction between epoxy resin and unsaturated carboxylic acid. In the present study, bis-phenol A based epoxy resin and methacrylic acid was used to produce vinyl ester resin. The reaction was conducted under both stoichiometric and non-stoichiometric conditions in the presence of triphenylphosphine as catalyst. The stoichiometric and non-stoichiometric experiments were conducted at 95, 100, 105 and 110℃ and at 90 and 95℃, respectively. The first order rate equation and mechanism based rate equation were examined. Parameters are evaluated by least square method. A comparison of mechanism based rate equation and experimental data show an excellent agreement. Finally, Arrhenius equation and activation energy were presented.