PC钢棒的延迟断裂及其原因分析 被引量:10

Delayed fracture of steel bar for prestressed concrete and its failure analyses
下载PDF
导出
摘要 介绍了PC钢棒延迟断裂的特征及机理,分析了诱发PC钢棒延迟断裂的材料缺陷.为消除PC钢棒延迟断裂的材料缺陷,提出了改善PC钢棒用30MnS i盘条质量的工艺措施. The features and mechanism of fracture of steel bar for prestressed concrete ( PC bars) are described, and the material defects which induced the delayed fracture in the PC bars are analyzed in the paper. In order to eliminate these defects, measures of improving the quality of 30MnSi rod coil are proposed.
出处 《南方金属》 CAS 2006年第6期35-38,共4页 Southern Metals
关键词 PC钢棒 延迟断裂 缺陷 steel bar for prestressed concrete delayed fracture defects
  • 相关文献

参考文献1

二级参考文献7

  • 1邢献强.PHC管桩钢丝滞后断裂原因初探[J].金属制品,1995,21(5):32-33. 被引量:2
  • 2松山晋作.延迟破坏[M].日本:日刊工业新闻社,1989.46-90.
  • 3木村利光.延迟破环解释的新进展[M].日本钢铁协会,1993.230.
  • 4高井健一.高强度钢的延迟破坏特征以及Si、Ca复合添加的影响[J].铁匕钢,1993,79(6):67-67.
  • 5M NAGUUMO. Function of Hydrogen in Embrittement of High-Strength Steels. ISIJ International,2001,6:592.
  • 6Reporton Prestressing Steel:5," Stress Corrosion Cracking Resistance Test for Prestressing Tendons" 1980, FIP.
  • 7阮起楠.高强度低松弛管桩钢筋的发展及质量现状[J].金属制品,2000,26(6):45-48. 被引量:5

共引文献14

同被引文献12

引证文献10

二级引证文献14

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部