载银纳米磁粒抗菌剂的研究 被引量:1

Study on antimicrobial materials of magnetic nanoparticles loaded silver
下载PDF
导出
摘要 采用双层包裹法首次制备出载银磁粒抗菌剂。并对样品进行SEM、XRD、IR、磁性参数分析和抗菌性能研究,结果显示磁粒抗菌剂的平均粒径为75nm,粒径均匀,基本呈圆球型。二氧化硅以无定形状态存在,银以银单质出现在纳米粉体中。磁粒抗菌剂的饱和磁化强度比纳米铁氧体减小,但仍具有好的磁性。银含量>3.87%时,对大肠杆菌和金黄色葡萄球菌都有99.9%的杀菌性能。 Antimicrobial materials of magnetic nanoparticles loaded silver was prepared by double-coating methods. The characterizations of products were investigated using X-ray diffraction (XRD),scanning electron microscopy (SEM),infrared spectroscopy (IR),energy dispersion spectrometry (SEM-EDS) and vibrating sample magnetometer(VSM). The results showed Ag/SiO2-coated CoFe2O4 nanopartieles were approximately spherical particles with an average diameter of 75 nm. The silica present in the product is amorphous and with simple silver phase based on the analyses of XRD. The magnetic parameters showed after coating the saturation magnetization decrease. When the content of silver is more than 3.87 %, the efficiency of sterilization of Ag/SiO^-coated CoFe^O4 was above 99.9% against staphylococcus aureus and escherichia coli.
出处 《功能材料》 EI CAS CSCD 北大核心 2006年第12期1870-1872,共3页 Journal of Functional Materials
基金 国家高技术研究发展计划(863计划)资助项目(2001AA218011)
关键词 抗菌剂 磁性 纳米 antimicrobial agent magnetic nanopartlcles silver
  • 相关文献

参考文献11

  • 1Percival S L,Bowler P G,Russell D.[J].Journal of Hospital Infection,2005,60(1):1-7.
  • 2Vernè E,Nunzio S D,Bosetti M,et al.[J].Biomaterials,2005,26(25):5111-5119.
  • 3Blaker J J,Nazhat S N,Boccaccini A R.[J].Biomaterials,2004,25(7-8):1319-1329.
  • 4Li Y,Leung P,Yao L,et al.[J].Journal of Hospital Infection,2006,62(1):58-63.
  • 5Shanmugam S,Viswanathan B,Varadarajan T K.[J].Materials Chemistry and Physics,2006,95(1):51-55.
  • 6Samuel U,Guggenbichler J P.[J].International Journal of Antimicrobial Agents,2004,23(1):75-78.
  • 7Cho K H,Park J,Osaka T,et al.[J].Electrochimica Acta,2005,51(5):956-960.
  • 8Peng B,Yuan C,Chai L Y,et al.[J].Trans.Nonferrous Met Soc China,2005,15(5):1156-1160.
  • 9Xiao X X,Huang K L,et al.[J].J Cent South Univ,2005,36(1):65-68.
  • 10Matsuura T,Abe Y,Sato Y,et al.[J].Journal of Dentistry,1997,25(5):37312.

同被引文献14

  • 1程晓敏,丁利,李万里,张小明.聚酰胺1010/Ag复合薄膜的制备与微结构[J].应用科技,2007,34(5):61-64. 被引量:1
  • 2张靖峰,杜志平,赵永红,台秀梅.纳米Ag/ZnO光催化剂及其催化降解壬基酚聚氧乙烯醚性能[J].催化学报,2007,28(5):457-462. 被引量:20
  • 3Huheen J C, Young M A, Van Duyne R P. Surface-enhanced hyper-raman scattering (SEHRS) on Ag film over nanosphere (FON) electrodes: Surface symmetry of centrosymmetric adsorbates[J]. Langmuir, 2006, 22 (25): 10354-10364.
  • 4Braun G, Pavel L, Morrill A R, et al. Chemically patterned mierospheres for controlled nanoparticle assembly in the construction of SERS hot spots [J]. J Am Chem Soc, 2007, 129:7760-7761.
  • 5Lim P Y, Liu R S, She P L, et al. Synthesis of Ag nanospheres particles in ethylene glycol by electrochemical-assisted polyol process[J]. Chem Phys Lett, 2006, 420:304-308.
  • 6Mohammed H S, Shipp D A. Uniform sub micron polymer spheres coated with Ag nanoparticles[J]. Maeromol Rapid Commun, 2006, 27:1774-1778.
  • 7Chen Z M, Gang T, Zhang J H, et al. Ag nanoparticles coated silica-PMMA core-shell microspheres andhollow PMMA microspheres with Ag nanoparticles in the interior surfaces[J]. Colloids and Surfaces A: Physicochem Eng Aspects, 2006, 272,151-156.
  • 8Chen C W, Chen M Q, Serizawa T, et al. in--situ synthesis and the catalytic properties of platinum colloids on polystyrene microspheres with surface grafted poly(N-isopropylacrylamide) [J]. Chem Commun, 1998, 831-832.
  • 9Chen C W, Tano D, Akashi M, et al. Colloidal platinum nanopartieles stabilized by vinyl polymers with amide side chains: Dispersion stability and catalytic activity in aqueous electrolyte solutions [J]. Journal of Colloid and Interface Science,2000,225:349-358.
  • 10Lee J M, Kim D W, Lee Y H, et al. New approach for preparation of silver-polystyrene heterogeneous nanocomposite by polyol process[J]. Chem Lett, 2005, 34(7) :928-929.

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部