W/ Cu functionally gradient materials （FGMs） containing 1% La2O3 and 1% TiC were prepared using graded sintering under tdtra-high pressure （GSUHP）. The specimens have been found to exhibit low porosity （11.57% and 11.35%, respectively）. Shearing strength of the specimens between layers is good. Moreover, the specimens have still demonstrated good performance in testing thermal-shock resistance. When power density of laser is 200MWm^-2, the specimens have been tested for thermal-shock resistance （1000 times）; the specimens that contained 1%La2O3 were not subjected to damage, whereas those that contained 1%TiC began to crack. Finally, effect of additives on thermal-shock resistance was also preliminarily discussed.
W/ Cu functionally gradient materials （FGMs） containing 1% La2O3 and 1% TiC were prepared using graded sintering under tdtra-high pressure （GSUHP）. The specimens have been found to exhibit low porosity （11.57% and 11.35%, respectively）. Shearing strength of the specimens between layers is good. Moreover, the specimens have still demonstrated good performance in testing thermal-shock resistance. When power density of laser is 200MWm^-2, the specimens have been tested for thermal-shock resistance （1000 times）; the specimens that contained 1%La2O3 were not subjected to damage, whereas those that contained 1%TiC began to crack. Finally, effect of additives on thermal-shock resistance was also preliminarily discussed.