醋酸乙烯与双环戊二烯顺丁烯二酸单酯的共聚 被引量:4

Co-polymerization of vinyl acetate and DHCM
下载PDF
导出
摘要 By using dicyclopentadiene reacting with maleic acid, dicyclopentadiene maleate (DHCM) was synthesized and its structure was characterized with IR and NMR spectrum.The co-polymerization of vinyl acetate and DHCM was studied at 70℃.The structure and particle morphology of the co-polymer were characterized with IR and TEM.The effects of DHCM content on the monomer conversion and average particle size were investigated.The results showed that when DHCM content was 2%(mass), the synthesized latex was of high conversion efficiency, small particle size and good stability. By using dicyclopentadiene reacting with maleic acid, dicyclopentadiene maleate (DHCM) was synthesized and its structure was characterized with IR and NMR spectrum. The co-polymerization of vinyl acetate and DHCM was studied at 70℃. The structure and particle morphology of the co-polymer were characterized with IR and TEM. The effects of DHCM content on the monomer conversion and average particle size were investigated. The results showed that when DHCM content was 2% (mass), the synthesized latex was of high conversion efficiency, small particle size and good stability.
出处 《化工学报》 EI CAS CSCD 北大核心 2007年第2期518-521,共4页 CIESC Journal
关键词 乳液聚合 醋酸乙烯 双环戊二烯 双环戊二烯顺丁烯二酸单酯 emulsion polymerization vinyl acetate dicyclopentadiene dicyclopentadiene maleate
  • 相关文献

参考文献11

二级参考文献15

共引文献48

同被引文献42

  • 1黄亚文.快干瓦楞纸箱淀粉粘合剂的研制[J].中国包装工业,2004,12(6):48-50. 被引量:1
  • 2肖淑红,王绪江.低温催化法合成双环戊二烯改性不饱和聚酯树脂[J].热固性树脂,2004,19(6):8-11. 被引量:8
  • 3孙文兵.改善聚醋酸乙烯酯胶膜耐水性的方法[J].胶体与聚合物,2005,23(3):35-36. 被引量:5
  • 4李敏,苏涛,郭立强,腊明.淀粉醋酸酯与醋酸乙烯接枝共聚制备白乳胶[J].中国胶粘剂,2005,14(10):24-26. 被引量:7
  • 5Naruhito Hori,Kentaro Asai,Akio Takemura.Effect of the ethylene/vinyl acetate ratio of ethylene-vinyl acetate emulsion on the curing behavior of an emulsion polymer isocyanate adhesive for wood[C].The Japan Wood R.esearch Society,2008,54:294-299.
  • 6陈月辉.改性耐水耐低温白乳胶及其制备方法[P].CN:02111292.4,2002.
  • 7Bassett D R,Sherwin M A.Crosslingking studies of thermosetting emulsion polymers[A].Waterborne and Higher Solids Coatings Symposium of the Southern Society of Coatings Technology[C].New Orleans,LA,1977.
  • 8Krishnan S,Klein A,El-Aasser M S,et al.Influence of a chain transfer agent on the crosslinking of poly(n-butyl methacrylate-co-methylol acrylamide) latex particles and films[J].Macromolecules,2003,36:3511-3518.
  • 9Nicole R Brown,Charles E Frazier.Cross-linking poly[(vinyl acetate)-co-N-methylolacrylamide] latex adhesive performanece part Ⅱ:Nmethylolacrylamide(NMA)distribution[J].Adhesion & Adhesives,2007,27:547-553.
  • 10Nicole R Brown,Joseph R Loferski,Charles E Frazier.Cross-linking poly(vinyl acetate-co-Nmethylolacrylamide) latex adhesive performance Part Ⅱ:Fracture mechanics and microscopic durability studies[J].International Journal of Adhesion & dhesives,2007,27:554-561.

引证文献4

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部