摘要
Sulfonated poly（phthalazinone）s （SPPENK, SPPESK and SPPBEK） were prepared by direct polymerization reaction from sulfonated monomers. The novel acid-base membranes were composed of sulfonated polymers as the acidic compounds, and polyetherimide （PEI） as the basic compounds, casting from their N-methylpyrrolidone （NMP） solution directly onto clean glass plates at 60 ℃ aiming at enhancing membrane toughness and other relative properties. The resulted acid-base composite membranes had excellent resistance to swelling, thermo-stability, hydrolysis resistance and oxidative resistance properties with highly ion-exchange capacity （IEC）.
Sulfonated poly（phthalazinone）s （SPPENK, SPPESK and SPPBEK） were prepared by direct polymerization reaction from sulfonated monomers. The novel acid-base membranes were composed of sulfonated polymers as the acidic compounds, and polyetherimide （PEI） as the basic compounds, casting from their N-methylpyrrolidone （NMP） solution directly onto clean glass plates at 60 ℃ aiming at enhancing membrane toughness and other relative properties. The resulted acid-base composite membranes had excellent resistance to swelling, thermo-stability, hydrolysis resistance and oxidative resistance properties with highly ion-exchange capacity （IEC）.
基金
This study was supported by the National Natural Science Foundation of China （No. 50373005）；the Chinese National Programs for High Technology Research and Development （＂863＂ plan, No. 2003AA33G030）.