在多孔α-Al_2O_3陶瓷管上制备β沸石膜的研究 被引量:1

Studies on the Preparation of Beta Zeolite Membrane on Porous α-Al_2O_3 Tubes
下载PDF
导出
摘要 以TEAOH(四乙基氢氧化铵)为模板剂,采用预涂晶种的二次水热合成法在平均孔径3~5μm的多孔α-Al2O3管状载体的外表面制备了连续致密的β沸石膜,并且用SEM,XRD和气体渗透对所合成的膜进行了表征,结果表明,所合成的膜连续致密,与载体管结合良好,没有大的缺陷。 The beta zeolite membranes were prepared on seeded α-Al2O3 substrate tubes with a mean pore size of 3-5 μm by the method of secondary .hydrothermal growth using TEAOH as templates. The prepared membranes were characterized with XRD, SEM and nitrogen permeance. XRD patterns show that the prepared membranes possess typical beta zeolite structure. SEM images indicated that a continuous and dense zeolite membrane with around 10 μm in thickness is formed on the seeded supports. Nitrogen permeation experiments proved that the permeation governed by surface diffusion. Thus the prepared membranes have no large defects.
出处 《硅酸盐通报》 CAS CSCD 北大核心 2007年第2期226-229,共4页 Bulletin of the Chinese Ceramic Society
基金 国家自然科学基金资助项目(No.20176004)
关键词 β沸石膜 管状载体 晶种法 beta zeolite membrane tubular supports seeded method
  • 相关文献

参考文献14

  • 1Wadlinger R L,Kerr G T,Rosinski E J.Catalytic composition of a crystalline zeolite[P].US Pat:3,308,069,19067.
  • 2Treacy M M.,Newsam J M.Two new three-dimensional twelve-ring zeolite frameworks of which zeolite beta is a disordered intergrowth[J].Nature,1988,322:249-251.
  • 3Higgins J B,Lapierre R B,Schlenker J L,et al.The framework topology of zeolite beta[J].Zeolites,1988,8:446-452.
  • 4Kiricsi I,Flego C,Pazzucoui G,et al.Progress toward understanding zeolite/3 acidity:an IR and 27Al NMR spectroscopic study[J].Phys Chem,1994,98:4627-4634.
  • 5Corma A,Martinez A,Monteiro J I F,et al.Isobutane/2-butene alkylation on zeolite beta:Influence of post-synthesis treatments[J].Appl Catal A,1996,142:139-146.
  • 6Zhang X F,Zhu W Q,Liu H O,et al.Novel tubular composite carbon-zeolite membranes[J].Materials letters,2004,58:2223-2227.
  • 7李永生,王金渠,鲍钟瑛,郭树才.在载体上引入晶种合成ZSM-5沸石膜[J].石油学报(石油加工),2000,16(5):31-35. 被引量:10
  • 8成岳,王连军,李健生,孙秀云.浸涂晶种法合成ZSM-5分子筛膜及气体渗透性能研究[J].硅酸盐通报,2005,24(3):102-105. 被引量:2
  • 9黄双艳,李永红,张玲,孙莹.基材表面性质对合成支撑β-沸石膜的影响[J].硅酸盐通报,2004,23(2):21-24. 被引量:2
  • 10李云华,黄双艳,李永红,何菲.载体的预处理对β沸石膜形成的影响[J].化学工业与工程,2004,21(2):79-83. 被引量:9

二级参考文献36

  • 1樊拴狮,史小农,李春华,王金渠.多孔载体上制备ZSM-5沸石膜的研究[J].石油化工,1995,24(5):321-323. 被引量:2
  • 2[1]Sano T, Yanagishita H, Kiyozumi Y, et al. Separation of ethanol/water mixture by silicalite membrane on pervaporation[ J ]. J Membr Sci, 1994, 95: 221 - 228.
  • 3[2]van der Puil A N, Dautzenberg A F M, van Bekkum H, et al. Preparation and catalytic testing of zeolite coatings on preshaped alumina supports [ J ]. Microporous and Mesoporous Mater, 1999,27:95 - 106.
  • 4[3]Sano T, Hasegawa M, Ejiri S, et al. Improvement of the pervaporation performance of silicalite membranes by modification with a silane coupling reagent [ J ]. Microporous Mater, 1995,5:179 - 183.
  • 5[4]Chiou Y H,Tsai T G,Sung S L, et al. Synthesis and characterization of zeolite (MFI) membrane on anodic alumina [J]. J Chem Soc Faraday Trans,1996,92:1061- 1066.
  • 6[5]Valtchev V, Mintova S. The effect of the metal substrate composition on the crystallization of zeolite coatings[J ].Zeolites, 1995,15:171 - 175.
  • 7[6]Vroon Z A E P,Keizer K,Burggraaf A J,et al. Preparation and characterization of thin zeolite MFI membranes on porous supports[ J ]. J Membr Sci, 1998,144: 65 - 76.
  • 8APELIAN MINAS R, FUNG ANTHONY S. Dealumination of zeolite β via dicarboxylic acid treatment [ J ]. Journal of Physical Chemistry, 1996,100(41 ) : 16 577 - 16 583.
  • 9HIROFUMI HAYASHIBARA, ATORU NISHIYAMA. The effect of alkali promoters on Cu - Na - ZSM - 5 catalysts in the oxidation of benzyl alcohol[J].Journal of Catalysis,1995. 153:254 - 264.
  • 10Lai R,Chem Mater,1998年,37卷,4275页

共引文献19

同被引文献16

  • 1张海娇,姚明恺,谢伟,刘月明,吴鹏.TS-1分子筛的无机法合成及其催化苯酚羟基化性能[J].催化学报,2007,28(10):895-899. 被引量:10
  • 2Balducei L, Bianchi D, Bortolo R, et al. Direct oxidation of benzene to phenol with hydrogen peroxide over a modified titanium silicalite[ J]. Angewandte Chemie International Edition,2003,42:4937-4940.
  • 3Bellussi G ,Rigutto M S. Metal-ions associated to the molecular sieve framework possible catalytic oxidation sites[ J ]. Stud~ it,. Surface Science and Catalysis, 1994,85 : 177-213.
  • 4Li G, Wang X S, Yan H S,et al. Effect of sodium ions on propylene epoxidation catalyzed by titanium silicalite[ J ]. Applied Catalysis A : General, 2001,218:31-38.
  • 5Zhang X F,Liu H 0 ,Yeung K L. Influence of seed size on the formatidn and mierostrueture of zeolite silicalite-1 membranes by seeded growth[ J]. Materials Chemistry and Physics ,2006,96( 1 ) :42-50.
  • 6Zhang X F,Wang J Q,Liu H O,et 81. Factors affecting the synthesis of hetero-atom zeolite Fe-ZSM-5 membrane[J]. Separation and Purification Technology,2003,32 : 151-158.
  • 7Wang X B, Zhang X F, Liu H O, et al. Preparation of titanium silicalite-I catalytic flints and application as catalytic membrane reactors [ J ], Chemical Engineering Joural,2010,156( 3 ) : 562-570.
  • 8Wang X B,Zhang X F, Wang Y, et al. Performance of TS-l-coated structured packing materials for styrene oxidation reaction [ J ]. ACS Catalysis, 2011,1:437-445.
  • 9Chert X S, Chert P, Kita H. Pervaporatian through "PS-1 membrane[ J ]. Microporous and Mesoporous Materials ,2008,115 : 164-169.
  • 10Meng L,Jiang H, Chen R Z, et al. Template-free synthesis of TS-1 zeolite film on tubular mullite support[ J]. Applied SuoCace Science ,2011,257 : 1928-1931.

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部