试样尺寸对定向合金DZ125热机械疲劳寿命的影响 被引量:5

Effects of Specimen Dimension on Thermomechanical Fatigue Life in DS Superalloy DZ125
下载PDF
导出
摘要 对DZ125定向凝固铸造镍基高温合金进行了三种相位和两种试样尺寸的热机械疲劳实验研究。实验结果表明:在热机械载荷下,试样表面和内部温度梯度以及蠕变和氧化损伤的存在,导致试样工作段直径影响热机械疲劳寿命。当应变水平较高(疲劳寿命较短)时工作段直径为8mm试样的疲劳寿命和工作段直径为6mm试样的疲劳寿命无明显差别。当应变水平较低(疲劳寿命较长)时工作段直径为8mm试样的疲劳寿命比工作段直径为6mm试样的疲劳寿命长。 Thermomechanical fatigue(TMF) life of three temperature-strain phase angles and two specimen dimensions was studied in directional solidification (DS) superalloy DZ125. The results showed that fatigue, creep and oxidation damage always developed during TMF,temperature gradient occurred on surface and inside of specimen. Specimen dimension affected TMF life in DS superalloy DZ125. At high strain levels with shorter fatigue life, there were no evidence difference between TMF life of 8mm diameter specimen and fatigue life of 6mm diameter specimen. At low strain levels with longer fatigue life,TMF life of 8mm diameter specimen is longer than that of 6mm diameter specimen.
出处 《材料工程》 EI CAS CSCD 北大核心 2007年第5期28-30,35,共4页 Journal of Materials Engineering
关键词 热机械疲劳 尺寸 蠕变 氧化 损伤 寿命 thermomechanical fatigue dimension creep oxidation damage life
  • 相关文献

参考文献9

二级参考文献32

  • 1何玉怀.Ni3Al合金热/机械疲劳裂纹扩展行为研究[M].北京:北京航空材料研究院,2000..
  • 2.金属力学性能试样(Q/6S 977-91)[R].北京:航空航天部第六二一研究所,1992..
  • 3张国栋.[D].北京:北京航空材料研究院,2002.
  • 4[3] UDOGUCHI T, WADA T. Thermal effect on low-cycle fatigue strength of steel. In: LITTLER D J eds. Thermal Stresses and Thermal Fatigue. London,1969.109-123.
  • 5[4] TARIS S, FUJINO M, HAJI T. Effect of mean temperature range on thermal fatigue strength of low carbon steel. J. Society Materials Science, Japan, 1973, 22:35.
  • 6[5] BEILING J, SLOT T. Effect of temperature and strain rate on low cycle fatigue resistance of AISI 304, 316 and 348 stainless steels. In: Fatigue at high temperature. ASTM STP 459. Lutharville-Timonium:1969:3-30.
  • 7[7] Engler-Pinto C C, Rezai-Aria F. Out-of-phase and in-phase thermo-mechanical fatigue behavior of IN738LC. Fatigue'96, 1996,2:831-836.
  • 8[9] JOOS R, ELZEY D M, ARZT E. Damage Mechanisms in an ODS-superalloy during isothermal and thermal-mechanical fatigue. In: BACHHELET E, BRUNETAUD R, COUTSOURADIS D eds. High temperature materials for power engineering. The Netherlands: Kluwer Academic, 1990,2,1173-1184.
  • 9[10] STRANGMAN T E. Thermal-mechanical fatigue life model for coated superalloy turbine components. Superalloys 1992. The Minerals Metals & Materials Society, 1992.795-804.
  • 10[11] REMY L. Fatigue life prediction under thermal-mechanical loading in a nickel-base superalloy. In: Thermo-mechanical fatigue behavior of materials, ASTM committee E9 on fatigue. ASTM STP 1186, 1993.3-16.

共引文献32

同被引文献37

引证文献5

二级引证文献33

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部