TiAl/40Cr扩散焊界面质量的超声评价 被引量:5

Ultrasonic evaluation of interface quality of TiAl and 40Cr diffusion welding
下载PDF
导出
摘要 采用超声C扫描法对TiAl和40Cr扩散焊界面进行了检测,分别研究了界面回波幅度平均值和标准差与接头抗剪强度之间的关系,并讨论了焊接温度和试样表面粗糙度对上述关系的影响及界面气隙长度与回波幅度的关系。结果表明,当试样表面粗糙度一致时,回波幅度平均值和标准差随着抗剪强度的降低而增加。表面粗糙度会影响回波幅度平均值和标准差与接头抗剪强度的关系。当空气间隙的长度小于400μm时,回波幅度与空气间隙长度近似成正比例关系。 The quality of TiAl and 40Cr diffusion welding interface was inspected by ultrasonic C-scan method and the relationships between mean and standard deviation of amplitude of interface echo and shear strength were studied.The effects of weld temperatures and surface roughnesses of specimens on above-mentioned relationships were investigated and the relationship between the amplitude and length of air gap was discussed.It is found that at a given surface roughness,bonding strength increases with the decreasing of mean and standard deviation of amplitude.The relationships between mean and standard deviation of amplitude of interface echo and shear strength are influenced by surface roughness.When the length of air gap is shorter than 400 μm,the amplitude of interface echo is approximately in proportion to the length of air gap.
作者 栾亦琳 刚铁
出处 《焊接学报》 EI CAS CSCD 北大核心 2007年第5期69-72,共4页 Transactions of The China Welding Institution
关键词 超声波检测 C扫描 扩散焊接 异种材料 ultrasonic test C-scan diffusion welding dissimilar materials
  • 相关文献

参考文献6

  • 1Nagy P B,Adler L.Ultrasonic evaluation of solid-state bonds[J].Materials Evaluation,1992,50(11):1328-1337.
  • 2Kato H,Abe S.Ultrasonic evaluation of the bonding strength of dissimilar metal bonds[J].NDT and E International,1996,29(6):355-361.
  • 3Katoh M,Nishio K,Yamaguchi T.Materials evaluation of diffusion bonded steel bar and its impact characteristics[J].NDT and E International,2002,35(4):263-271.
  • 4Gang T,Takahashi Y.Ultrasonic echo signal features of dissimilar material bonding joints[J].Transaction of Nonferrous Metals Society of China,2004,14(6):1050-1054.
  • 5刘松平,郭恩明,王瑞川,谢凯文,张斌,侯冠群,Vadim M.Levin,Petronyuk S.Julia.钛合金扩散连接界面完整性超声定量评估[J].航空制造技术,2003,46(5):32-36. 被引量:3
  • 6Cheng A,Deutsch W.Characterization of diffusion bonds of titanium plates using transmitted ultrasonic signals[J].NDT and E International,1998,31(3):175-182.

二级参考文献3

  • 1MatsonDM.Ultrasonicinspectionofdiffusionbondedplateletrocketchamberliner[].MaterialsEvaluation.1993
  • 2WegleinRD.Titaniumdiffusionbondevaluationviaac ousticmicroscopy[]..1988
  • 3LiuSongping,LevinVM,GuoEnming.Acousticimag ingofmicrostructuresofcarbonfiber reinforcedcompositelami nates[]..2001

共引文献2

同被引文献52

  • 1黄江,李坚,刘伟平.水浸聚焦探头声透镜的研制[J].南昌航空大学学报(自然科学版),2003,19(4):86-89. 被引量:2
  • 2史鸿培.异材热等静压扩散焊接[J].宇航材料工艺,1993,23(5):41-45. 被引量:1
  • 3陈志强,李亮,冯建春.高能射线工业CT最新进展[J].CT理论与应用研究(中英文),2005,14(4):1-4. 被引量:19
  • 4毛健,江武祥,呼和,杨万宏,吴仲棠.双合金热等静压复合工艺研究[J].航空材料学报,1996,16(4):7-12. 被引量:7
  • 5轩福贞,张波,李淑欣.电阻法用于扩散焊接头微孔缺陷评价的数值模拟[J].焊接学报,2007,28(4):9-12. 被引量:5
  • 6周武平,车洪艳,刘国辉,等.热等静压扩散连接技术的研究及应用[C]//2012年第二届中国粉末冶金产业发展论坛论文集.上海,2012:65-70.
  • 7Tanabe J, Sasaki T, Kishi S. Diffusion Bonding of Ti/Graphite and Ti/Diamond by Hot Isostatic Pressing Method[J]. Journal of Materials Processing Technology, 2007, 192/193: 453-458.
  • 8Hunt R M, Goods S H, Ying A, et al. Evaluation of Cu as an In- terlayer in Be/F82H Diffusion Bonds for ITER TBM[J]. Jour- nal of Nuclear Materials, 2011, 417: 89-92.
  • 9Stepanskj L G, Simunina T A. A Temperature Calculation for Metal Surface During Hot Pressure of Steel and Titanium Profiles [J] .Kuznechno-Shtampovochnoe Proizvodstvon, 1993(3): 3-5.
  • 10Laptev Alexander M, Samarov Victor N. Theory of Hot Isostat- ic Pressing and Its Application Forcalculation of Powder Com- paction at High and Low Pressures[C]//Compaetion and Other Consolidation Processes Advances in Powder Metallurgy. Princ- eton NJ, USA: Metal Powder Industries Federation, 1992: 465- 473.

引证文献5

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部