航空用超高强度钢中夹杂物导致疲劳裂纹萌生与扩展的微观行为 被引量：5

Study on Inclusion Induced Fatigue Crack Initiation and Propagation in Ultra-High Strength Steel for Aerospace Application
下载PDF
导出
摘要 采用扫描电镜原位观测的方法,跟踪观察了低周疲劳载荷下航空用超高强度钢MA250中夹杂物导致裂纹萌生与扩展的微观行为,得到了MA250钢低周疲劳裂纹萌生与扩展的基本特性,讨论了精确测定MA250钢疲劳裂纹扩展速率的方法。 The micro-behavior of inclusion inducing crack initiation and propagation in ultra-high strength steel MA250 for aerospace application under low cyclic fatigue loading was studied by means of SEM original position observation. The characteristics of low cyclic fatigue crack initiation and propagation were obtained. The method for accurately measuring fatigue crack growth rate in MA250 is discussed.
作者 范红妹 曾燕屏 王习术 崔正强 谢锡善
机构地区 北京科技大学高温合金研究室 清华大学工程力学系
出处 《钢铁》 CAS CSCD 北大核心 2007年第7期72-75,86,共5页 Iron and Steel
关键词 超高强度钢 夹杂物 裂纹萌生和扩展 断裂 ultra-high strength steel inclusion crack initiation and propagation fracture
分类号 TG142.13 [金属学及工艺—金属材料]
  • 相关文献

参考文献13

  • 1李守新.夹杂对高强钢疲劳性能影响的研究[J].中国基础科学,2005,7(4):14-15. 被引量：20
  • 2Murakami Y.Metal Fatigue;Effects of Small and Defects Nonmetallic Inclusions[M].UK:Elservier,2002.
  • 3Maropoulos S,Ridley N.Inclumons and Fracture Characteristies of HSLA Steel Forgings[J].Material Science and Engineering,2004,384A(1-2):64-69.
  • 4YANG Z G,YAO G,LI G Y,et al.The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42CrMoVNb Steel[J].International Journal of Fatigue,2004,26(9):959-966.)
  • 5王习术,梁锋,曾燕屏,谢锡善.夹杂物对超高强度钢低周疲劳裂纹萌生及扩展影响的原位观测[J].金属学报,2005,41(12):1272-1276. 被引量：65
  • 6Garrison Jr W M,Moody N R.The Influence of Inclusion Spacing and Microstructure on the Fracture Toughness of the Secondary Hardening Steel AF1410[J].Metallurgical Transactions,1987,18A(7):1257-1263.
  • 7WANG Q Y,Bathias C,Kawagoishi N,et al.Effect of Inclusion on Subsurface Crack Initiation and Gigacyde Fatigue Strength[J].International Journal of Fatigue,2002,24(12):1269-1274.
  • 8Barbangelo A.Influence of Nonmetallic Inclusions on Fatigue Crack Growth in a Structural Steel[J].Journal of Material Science,1985,20(6):2087-2092.
  • 9Chapetti M D,Tagawa T,Miyata T.Ultra-Long Cycle Fatigue of High-Strength Carbon Steel Part Ⅰ Review and Analysis of the Mechanism of Failure[J].Material Science and Engineering,2003,356 A(1-2):227-235.
  • 10Laz P J,Hillberry B M.Fatigue Life Prediction From Inclusion Initiated Cracks[J].Int J Faugue,1998,20(4):263-270.

二级参考文献9

共引文献81

同被引文献64

引证文献5

二级引证文献31

钢铁
2007年 第7期

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部