多孔纯钛种植体表面快速沉积钙磷涂层的研究 被引量:6

Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface
下载PDF
导出
摘要 商业纯钛片经磨平、喷砂、清洗、酸洗后分成A、B两组。A组不作任何处理,B组用H2SO4和HCl混合液酸蚀,然后两组钛片同时置于37℃的仿生液SBF-A中1d及SBF-B中2d。结果两组钛片表面均可沉积磷灰石涂层,涂层为多孔片状结构,X射线衍射分析证实其为碳酸化羟基磷灰石和磷酸八钙的混合物,钙磷原子量比约1.51。这说明在多孔纯钛表面可以快速仿生沉积碳酸化磷灰石涂层。 The aim of this study was to elaborate a dense, strong and thin calcium-phosphate coating on commercial porous pure titanium implant surface in the light of a fast biomimetic procedure. After being polished, sandblasted, cleaned and treated with the mixture of HF and HNO3, the titanium plates were divided into two groups,namely group A and group B. The specimens of group A were free from any treatment. The specimens of group B were treated with the mixture of 48%H2SO4 and 18%HCl. All specimens soaked in SBF-A solution for ld. Then the specimens were immersed in the SBF-B solution for 2 d. A thin calcium-phosphate coating was deposited on all the specimens of the two groups ,the surface consisted of well-formed crystals, which were proved to be the mixture of hydroxycarbonated apatite (HCA) and octacalcium phosphate (OCP) ; the coating's Ca/P rate was 1.51. A thin carbonated calcium-phosphate coating was deposited on porous pure titanium by the use of the fast biomimetic procedure.
出处 《生物医学工程学杂志》 EI CAS CSCD 北大核心 2007年第4期806-811,共6页 Journal of Biomedical Engineering
基金 浙江省医药卫生优秀青年科技人才专项科研基金资助项目(2004016) 浙江省科技计划重点项目资助(200523006)
关键词 纯钛 仿生液 钙磷涂层 Pure titanium Simulated body fluid(SBF) Calcium-phosphate coating
  • 相关文献

参考文献12

  • 1Albrektsson T,Wennerberg A.Oral implant surfaces:Part 1--review focusing on topographic and chemical properties of different surfaces and in vivo responses to them.Int J Prosthodont,2004;17(5):536
  • 2Yang Y,Kim KH,Ong JL.A review on calcium phosphate coatings produced using a sputtering process--an alternative to plasma spraying.Biomaterials,2005; 26(3):327
  • 3Habibovic P,Barrere F.biomimetic hydroxyapatite coating on metal implants.J Am Ceram Soc,2002; 85:517
  • 4Hench LL,Characterization of bioceramics.In:Hench LL,Wilson J,editors.An introduction to bioceramics.Singapore:World Science.1993:319-334
  • 5Barrere F,van BC.Nucleation of biomimetic Ca-P coatings on ti6A14V from a SBF×5 solution:influence of magnesium.Biomaterials,2002;23(10):2211
  • 6Barrere F,Snel MM.Nano-scale study of the nucleation and growth of calcium phosphate coating on titanium implants.Biomaterials,2004;25(14):2901
  • 7Kokubo T,Kim HM,Kawashita M,et al.Bioactive metals:preparation and properties.J Mater Sci Mater Med,2004;15(2):99
  • 8Wen HB,De Wijn JR,Liu Q,et al.A simple method to prepare calcium phosphate coatings on Ti6Al4V.J Mater Sci Mater Med,1997;8(12):765
  • 9Wen HB,Liu Q,De Wijn JR,et al.Preparation of bioactive microporous titanium surface by a new two-step chemical treatment.J Mater Sci Mater Med,1998;9(3):121
  • 10Jonasova L,Muller FA,Helebrant A,et al.Biomimetic apatite formation on chemically treated titanium.Biomaterials,2004;25(7-8):1187

同被引文献104

引证文献6

二级引证文献24

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部