用X射线应力测量仪分别测定了凸轮轴经滚压、喷丸和滚压加喷丸3种表面强化后的表面残余应力场分布,同时测定了凸轮轴在500℃退火处理后的残余应力松弛情况。试验结果表明,3种工艺处理后的残余应力均为压应力,滚压后凸轮轴的表面残压应力均较其余两者大,滚压应为凸轮轴最佳表面强化工艺;滚压加喷丸处理显著降低了滚压工件表面残余压应力,减弱了滚压工艺的效果。
The distributions of camshaft surface residual stress by rolling, peening and rolling＋peening were measured respectively with model X - 350A of XRD stress tester, and laxation complexions of camshaft residual stress by 500℃ anneal treatment were tested. The experimental results were shown that residual stresses by above three kinds of craft treatments were all compressive stress, and the surface residual stresses of camshaft by rolling were bigger than other treatment modes, which was the best surface strengthening craft for camshaft; rolling ＋ peening treatment has obviously decreased surface compressive residual stress on rolling pieces, which weakened rolling effect.
出处
《农业机械学报》
EI
CAS
CSCD
北大核心
2007年第8期173-176,共4页
Transactions of the Chinese Society for Agricultural Machinery
基金
江苏省2005年度研究生创新计划项目(项目编号:XM05-32)
关键词
凸轮轴
表面强化
残余应力
Camshaft, Surface strengthening, Residual stress