中厚钢板缺陷分析及原因探讨 被引量:14

Study of Flaws in Heavy and Medium Plate
下载PDF
导出
摘要 对不同厚度规格中厚钢板用超声波探伤观察到的缺陷统计和分析表明:中厚钢板内部缺陷为钢板厚度中心区域珠光体带中的微裂纹。位于偏析区内宽度超过25μm珠光体带中;裂纹源为珠光体带中MnS类型的塑性夹杂与钢基体的界面;裂纹的形成温度低于700℃,形成于轧后冷却或矫直阶段。铸坯中心线偏析是产生裂纹的内部条件,轧后冷却或矫直过程中的张应力是外部条件。 Flaws in the heavy and medium plate of different thickness detected by ultrasonic detector were studied. Conclusions are: firstly, flaws are caused by micro-cracks in the pearlite band at the center area of the plate; secondly, micro-cracks mostly appear in the pearlite band wider than 25 μm located in the centerline segregation area; thirdly, the interface between MnS type plastic inclusions and the matrix is the source of cracks; fourthly, micro cracks form after the hot rolling and at the temperature lower than 700 ℃. The internal condition for cracking is the centerline segregation of slab and the external is the tensile stress of slab formed during cooling or straightening.
出处 《钢铁》 CAS CSCD 北大核心 2007年第8期41-45,共5页 Iron and Steel
关键词 中厚钢板 超声波探伤 裂纹 heavy and medium plate ultrasonic flaw detecting crack
  • 相关文献

参考文献6

  • 1Ghosh A.Segregation in Cast Products[J].Sadhana,2001,26(1,2):5-24.
  • 2Jacobi Hatto F.Investigation of Centreline Segregation and Centreline Porosity in CC-Slabs[J].Steel Research International,2003,74(11-12):667-678.
  • 3Teruo Yamashita,Shiro Torizuka,Kotobu Nagai.Effect of Manganese Segregation on Fine-Grained Ferrite Structure in Low-Carbon Steel Slabs[J].ISIJ International,2003,43(11):1833-1841.
  • 4Majka T F,Matlock D K,Krauss G.Development of Microstructural Banding in Low-Alloy Steel With Simulated Mn Segregation[J].Metallurgical and Materials Transactions A,2002,33A(6):1627-1637.
  • 5Holby E,Smith J F.Lamellar Tearing -Problem Nobody Seems to Want to Talk About[J].Welding Journal,1980,(2):37-44.
  • 6Wilson W G.Minimizing Lamellar Tearing by Improving Z-Direction Ductility[J].Welding Journal,1974,(11):691-695.

同被引文献78

引证文献14

二级引证文献36

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部