应用无接触电阻率法研究矿渣水泥的早期水化 被引量:4

Study on Slag Cement at Early Hydration Stage by Contactless Resistivity Instrument
下载PDF
导出
摘要 通过电阻率变化探讨水泥水化早期阶段的特性。结果表明:在波特兰水泥中加入矿渣,电阻率先随矿渣掺量的增加而增加,水化1d后电阻率随掺量的增加而降低;当加入NaOH时电阻率先逐渐降到最小值,当水化进入到凝结硬化阶段,电阻率快速增加并超过波特兰水泥;当加入NaSO_4时电阻率发展早期比较平缓,后期有迅速的增加。对各试样的孔结构参数进行了测试,结果表明孔结构与电阻率有一定的对应关系。 The hydration characters of cements in early stage were studied by means of testing resistivity change. The results indicate that when adding slag to Portland cement, at first the resistivity increased with the augment of mixed slag amount, however after hydration for 1 d, the resistivity decreased with the increase of mixed slag amount. When NaOH was added, resistivity first fell to the minimum, then increased rapidly and exceeded that of Portland cement at hardening stage. When NaS04 was added, resistivity changed slowly at first and then rose rapidly. The pore structure parameters were determined and the results illuminated that there was some corresponding relation between pore parameters and resistivity.
出处 《硅酸盐通报》 CAS CSCD 北大核心 2007年第4期645-652,共8页 Bulletin of the Chinese Ceramic Society
基金 香港Grant Council资助项目(HKUST 6272/03E)
关键词 电阻率 孔结构 resistivity pore structure alkali
  • 相关文献

参考文献9

  • 1Tamas F D. Electrical conductivity of cement pastes [ J ]. Cem Concr Re-s, 1982,12 ( 1 ) : 115-120.
  • 2McCarter W J ,Afshar A B. Some aspects of the electrical properties of cement paste[ J]. J Mater Sci Lett, 1984,3( 12 ) : 1083-1086.
  • 3Tamas F D, Farkas E, Voros M, et al. Low-frequeney electrical conductivity of cement, clinker and clinker mineral pastes [ J ]. Cem Concr Res, 1987,17(2) :340-348.
  • 4Scuderi C A ,Mason T O ,Jennings H M. Impedance spectra of hydrating cement pastes[ J]. J Matt Sci ,1991,26(2 ) :349-353.
  • 5Li Z J, Li W L. Contactless, Transformer-based measurement of the resistivity of materials [ P]. US Patent, 6639401. 2003-10-28.
  • 6魏小胜,肖莲珍,李宗津.采用电阻率法研究水泥水化过程[J].硅酸盐学报,2004,32(1):34-38. 被引量:99
  • 7Zhang X, Ding X Z, Lim T H, et al. Microwave Study of Hydration slag cement blends in early period [ J ]. Cem Concr Res, 1995,25 (5) : 1086- 1094.
  • 8Salem T M, Ragai S M. Electrical conductivity of granulated slag cement kiln dust-silica fume pastes at different porosities [ J ]. Cem Concr Res, 2001,31 (5) :781-787.
  • 9Tumidajski P J. Relationship between resistivity, diffusivity and microstructural descriptors for mortars with silica fume[ J]. Cem Concr Res ,2005, 35(7) :1262-1268.

二级参考文献6

  • 1ARCHIE G E. The electrical resistivity log as an aid in determining some reservoir characteristics[J]. Trans Am Inst Min Metall Pet Eng, 1942,146:54-62.
  • 2McCARTER W J, BROUSSEAU R. The A.C. response measurements on cement paste[J]. Cem Concr Res, 1990, 20(6): 891-900.
  • 3GU P, XIE P, XU Z, et al. A rationalized AC impedance model for microstructural characterization of hydrating cement systems[J]. Cem Concr Res, 1993, 23(2): 359-367.
  • 4PETIN N, GAJSINOVITCH E. A study of the setting process of cement paste by electrical conductivity methods[J]. J Gener Chem USSR, 1932, 2:614-629.
  • 5LI Zongjin, LI Wenlai. Contactless, transformer-based measurement of the resistivity of materials[P]. US Patent, 6639401. 2003-10-28.
  • 6DAVID R L. Handbook of Chemistry and Physics[M]. 75th edition. Ohio, USA: CRC Press, 1996. p324.

共引文献98

同被引文献36

引证文献4

二级引证文献22

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部