搅拌时间对水合碳酸镁形貌和组成的影响 被引量:12

Influence of Stirring Time on the Morphology and Composition of Magnesium Carbonate Hydrates
下载PDF
导出
摘要 通过共沉淀法,研究了Mg(NO3)2·6H2O和K2CO3生成水合碳酸镁的形貌和组成随反应初始溶液搅拌时间的变化规律。结果发现,当反应初始溶液的搅拌时间在1~8min变化时,可使产物针状水合碳酸镁的直径控制在0.5~23μm,长度介于2~200μm;通过对产物组成的红外光谱和热重分析,发现当搅拌时间在1~20min变化时,所得产物MgCO3·xH2O(1〈x〈3)中的水分含量也随之发生较大变化。 Magnesium carbonate hydrates were facilely synthesized by the precipitation of Mg( NO3 )2 · 6H2O and K2CO3in aqueous solutions, and their morphologies and compositions were characterized by SEM, FTIR spectroscopy and TGA. SEM observation demonstrates that the needlelike magnesium carbonate hydrates with variable sizes, ranging from 0.5 to 23 μm in diameter and 2 to 200μm in length, can be synthesized by adjusting carefully the stirring time of the initial reaction solution in the range of 1 -8 min. IR and TG analyses indicate that the stirring time has a significant effect on the content of water of magnesium carbonate hydrates besides their morphologies, and the corresponding composition has a simple formula of MgCO3 · xH2O,in which the value of x is between 1 -3 with the variety of stirring time from 1 to 20 min.
出处 《精细化工》 EI CAS CSCD 北大核心 2007年第9期835-838,869,共5页 Fine Chemicals
基金 国家自然科学基金(20577050) 国家重点基础研究计划(2003CB415001)资助课题~~
关键词 水合碳酸镁 搅拌时间 形貌 组成 功能材料 magnesium carbonate hydrate stirring time morphology composition funcational materials
  • 相关文献

参考文献16

  • 1Freitag F, Kleinebudde P. How do roll compaction/dry granulation affect the tableting behaviour of inorganic materials? Comparison of four magnesium carbonates [ J ]. Euro J Pharm Sci,2003,19:281 - 289.
  • 2Botha A,Strydom C A. Preparation of a magnesium hydroxy carbonate from magnesium hydroxide [ J ]. Hydrometallurgy, 2001, 62 : 175 - 183.
  • 3Kloprogge J T, Martens W N, Nothdurft L, et al. Low temperature synthesis and characterization of nesquehonite[J]. J Mater Sci Lett,2003,22:825 - 829.
  • 4Choudhary V R, Pataskar S G, Gunjikar V G, et al. Influence of preparation conditions of basic magnesium carbonate on its thermal-analysis [J]. Thermochimica Acta, 1994,232 : 95 - 110.
  • 5Yan C L,Xue D F. Novel self-assembled MgO nanosheet and its precursors [ J]. J Phy Chem B,2005,109:12358 -12361.
  • 6王峰,孙思,郭锴.旋转填充床一次碳化法制备轻质碳酸镁[J].无机盐工业,2006,38(2):31-33. 被引量:8
  • 7Mitsuhashi K ,Tagami N, Tanabe K, et al. Synthesis of microtubes with a surface of " house of cards" structure via needlelike particles and control of their pore size [ J ]. Langmuir, 2005,21 : 3659 - 3663.
  • 8Wang X, Xue D. Direct observation of the shape evolution of MgO whiskers in a solution system [ J ]. Mater Lett, 2006,60 : 3160 -3164.
  • 9Zhang Z,Zheng Y,Ni Y ,et al. Temperature and pH dependent morphology and FTIR analysis of magnesium carbonate hydrates [ J]. J Phys Chem B ,2006,110 : 12969 - 12973.
  • 10Yang B, Kamidate Y, Takahashi K,et al. Unsteady stirring method used in suspension polymerization of styrene [J]. J Appl Polym Sci ,2000,78 : 1431 - 1438.

二级参考文献5

共引文献7

同被引文献125

引证文献12

二级引证文献69

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部