全层片组织 TiAl 基合金室温断裂机理的研究

THE ROOM TEMPERATURE FRACTURE MECHANISMS OF A FULLY LAMELLAR TiAl ALLOY
下载PDF
导出
摘要 在SEM和TEM下对Ti33Al3Cr0.5Mo合金全层片组织薄板状和薄膜状试样分别进行了动态拉伸,并原位观察了试样中裂纹的形核及扩展过程.发现裂纹遇到内相界面时会发生偏转或裂尖发生钝化;主裂纹主要以使剪切带断裂而与微裂纹相连接的方式扩展并沿曲折路径进行. The in situ tensile of a fully lamellar TiAl alloy, with a composition of Ti 33Al 3Cr 0 5 Mo(mass fraction %), was performed with plate and foil specimens in SEM and TEM respectively. The process of initiation and extension of crack was in situ observed. The results revealed that the crack would deflect and its tip would blunt when it met the interface; the extension of the main crack was performed by the shear ligments fracture to connect with microcrack; the extension of crack had the tortuous path.
出处 《中南工业大学学报》 CSCD 北大核心 1997年第2期152-155,共4页 Journal of Central South University of Technology(Natural Science)
基金 国家"八六三"高技术研究计划基金
关键词 TIAL 断裂机理 全层片组织 金属间化合物 TiAl based alloy fracture toughness fracture mechanisms fully lamellar composition
  • 相关文献

参考文献4

  • 1贺跃辉,中南工业大学学报,1996年,27卷,3期,300页
  • 2Chan K S,Metall Trans,1995年,26卷,A期,1407页
  • 3Chan K S,Metall Trans,1991年,22卷,A期,2021页
  • 4Feng C R,Scr Metall,1988年,22卷,1481页

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部