ZnO纳米片自组装空心微球的无模板水热法制备与发光性质 被引量:11

原文传递
导出
摘要 报道了一种简单的制备ZnO纳米片自组装成空心微球的无模板水热法.即通过醋酸锌与水和乙二醇混合溶剂(V水/V乙二醇=1/20)在100℃水热反应12h合成了ZnO空心微球.利用扫描电子显微镜、透射电子显微镜、X射线衍射仪和红外光谱对产物进行了表征和分析.结果表明,所制备ZnO空心微球的直径为2~5μm,它是由直径为10~20nm纤锌矿结构的ZnO纳米片自组装而成.研究了水与乙二醇的体积比及反应时间对产物形貌的影响,结果表明乙二醇在ZnO纳米片的形成与自组装过程中起着关键作用,并提出了可能的生长机理.在波长为300nm光的激发下,发现ZnO空心微球具有发光峰位于397nm强的紫外光发光和486nm弱的蓝绿光发光,这两种发光分别起源于ZnO宽带隙的激子发射和氧空位与间隙氧之间的跃迁.
出处 《中国科学(B辑)》 CSCD 北大核心 2007年第5期417-425,共9页 Science in China(Series B)
基金 国家自然科学基金(批准号:20573072) 教育部博士点基金(批准号:20060718010)资助项目
  • 相关文献

参考文献32

  • 1Gao S Y, Zhang H J, Wang X M, Deng R P, Sun D H, Zheng G L. ZnO-based hollow microspheres: Biopolymer-assisted assemblies from ZnO nanorods. J Phys Chem B, 2006, 110(32): 15847-- 15852.
  • 2Trivikrama Rao G S, Tarakarama Rao D. Gas sensitivity of ZnO based thick film sensor to NH3 at room temperature. Sens Actu B, 1999, 55(2-3): 166--169.
  • 3Pan Z W, Dai Z R, Wang Z L. Nanobelts of semiconducting oxides. Science, 2001, 291(9): 1947--1949.
  • 4Huang M H, Mao S, Feick H, Yan H Q, Wu Y Y, Kind H, Weber E, Russo R, Yang P D. Room-temperature ultraviolet nanowire nanolasers. Science, 2001, 292(5523): 1897--1899.
  • 5Wang Z L. Zinc oxide nanostructures: growth, properties and applications. J Phys: Condens Matter, 2004, 16(25): R829--R858.
  • 6Li F, Ding Y, Gao P X, Xin X Q, Wang Z L. Single-crystal hexagonal disks and rings of ZnO: Low-temperature, large-scale synthesis and growth mechanism. Angew Chem, 2004, 116(39): 5350--5354.
  • 7Fan Z Y, Wang D W, Chang P C, Tseng W Y, Lu J G. ZnO nanowire field-effect transistor and oxygen sensing property. Appl Phys Lett, 2004, 85(24): 5923--5925.
  • 8Wan Q, Li Q H, Chen Y J, Wang T H, He X L, Li J P, Lin C L. Fabrication and ethanol sensing characteristics of ZnO nanowire gas sensors. Appl Phys Lett, 2004, 84(18): 3654--3656.
  • 9Kang B S, Ren F, Heo Y W, Tien L C, Norton D P, Pearton S J. pH measurements with single ZnO nanorods integrated with a microchannel. Appl Phys Lett, 2005, 86(11): 112105(1-3).
  • 10Fan Z Y, Lu J G. Electrical properties of ZnO nanowire field effect transistors characterized with scanning probes. Appl Phys Lett, 2005, 86(3): 032111(1-3).

二级参考文献10

共引文献11

同被引文献224

引证文献11

二级引证文献33

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部