The effect of heat treatment and rolling process on the properties and microstructures of Ti-26(Ti-15V-3Al-3Cr-3Sn-Forming) sheet was studied. The results show that the best rolling temperature for Ti-26 alloy is in the temperature range from 900 ℃ to 950℃. Under this condition,the resistance of deformation and yield ratio are low and the alloy has better hot work ability. The alloy will achieve better mechanical properties and completely recrystallized β microstructure when the deformation ratio is not less than 60% and the solution temperature is 30 ℃ above the phase transformation temperature. The best heat treatment conditions are recommended as:790℃,30 min,AC or WQ followed by 510 ℃,10 h,AC. Under this heat treatment condition the strength of the Ti-26 alloy is 1 230 MPa and the elongation is 15%.
The effect of heat treatment and rolling process on the properties and microstructures of Ti-26 （Ti-15V-3Al-3Cr-3Sn-Forming） sheet was studied. The results show that the best rolling temperature for Ti-26 alloy is in the temperature range from 900 ℃ to 950℃. Under this condition, the resistance of deformation and yield ratio are low and the alloy has better hot work ability. The alloy will achieve better mechanical properties and completely recrystallized β microstructure when the deformation ratio is not less than 60% and the solution temperature is 30 ℃ above the phase transformation temperature. The best heat treatment conditions are recommended as： 790℃, 30 min, AC or WQ followed by 510 ℃, 10 h, AC. Under this heat treatment condition the strength of the Ti-26 alloy is 1 230 MPa and the elongation is 15%.
出处
《中国有色金属学会会刊：英文版》
CSCD
2007年第A01期532-536,共5页
Transactions of Nonferrous Metals Society of China
基金
Project(2007CB613807) supported by the National Basic Research Program of Chin
关键词
钛合金
热处理技术
金属材料
微观结构
Ti-26 titanium alloys
sheet material
heat treatment
rolling processing