摘要
Using the microwave sintering technology, the effects of phosphorus （P） additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only 0.3wt% P additions, full density WC-10Co cermets were obtained at temperature of 1250℃, which is 70 ℃ lower than that of the undoped counterparts. Lower sintering temperature can result in finer WC grain growth; therefore, the P-doped WC-10Co alloys exhibited higher hardness than the undoped ones. But at the same time, P doping could lead to sacrifice of fracture toughness ofWC-10Co cemented carbides.
Using the microwave sintering technology, the effects of phosphorus （P） additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only 0.3wt% P additions, full density WC-10Co cermets were obtained at temperature of 1250℃, which is 70 ℃ lower than that of the undoped counterparts. Lower sintering temperature can result in finer WC grain growth; therefore, the P-doped WC-10Co alloys exhibited higher hardness than the undoped ones. But at the same time, P doping could lead to sacrifice of fracture toughness ofWC-10Co cemented carbides.
基金
the National Key Technology R&D Program of MOST,China(2003BA328C)
the National Natural Science Foundation of China(50472043)
Natural Science Foundation of Hubei Province(2006ABA312,2006ABA316)