K405合金空心球泡沫的制备与压缩性能研究 被引量:3

Fabrication and Compressive Properties of K405 Alloy Hollow Sphere Foams
下载PDF
导出
摘要 采用空心球法制备平均孔径约3mm、壁厚约0.1mm的K405合金空心球泡沫。首先在聚苯乙烯球上涂覆粉浆制备湿球,将其按体心立方结构排布,随后在真空条件下将堆跺好的球坯在300℃保温40min分解有机物,在1150℃保温150min烧结。制备的K405合金空心球泡沫的密度分别为0.987,0.999和1.085g/cm3;压缩试验结果表明:该泡沫试样的变形行为基本一致,屈服强度大于25MPa。 K405 alloy hollow sphere foams with average aperture about 3mm and about 0.1mm wall thickness are fabricated by hollow sphere method. Firstly the wet spheres which were formed as powder shells from slurries by coating polystyrene cores, were arranged in the body-centered cubic (BCC) way. Subsequently, the spheres stacks were heat-treated in vacuum at 300 ℃ for 40 min to decompose the organic materials, sintered at 1150 ℃ for 150 min. The densities of the finished K405 alloy hollow sphere foams are 0.987, 0.999 and 1.085 g/cm^3 respectively. The results of compressive tests show that the deformation behaviors of K405 foam specimens are almost the same. The yield strengths are higher than 25 MPa.
机构地区 哈尔滨工业大学
出处 《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2008年第1期135-138,共4页 Rare Metal Materials and Engineering
关键词 空心球 金属泡沫 K405合金 hollow sphere metal foam K405 alloy
  • 相关文献

参考文献12

  • 1Banhart J.Progress in Material Science[J],2001,46:559
  • 2Gasser S et al.Advanced Engineering Materials[J],2004,6(1~2):97
  • 3Liu Peisheng(刘培生).Introduction to Cellular Materials(多孔材料引论)[M].Beijing:Tsinghua University Press,2003:160
  • 4Degischer H P et al.Translated by Zuo Xiaoqing(左孝青).Handbook of Cellular Metals(多孔泡沫金属)[M].Beijing:Chemical Industry Press,2005:48
  • 5Andersen B O et al.Adv Engineering Mater[J],2002,2(4):192
  • 6Gibson L J,Ashby M F.Translated by Liu Peisheng(刘培生).Cellular Solid:Structure and Properties(多孔固体结构与性能)[M].Beijing:Tsinghua University Press,2003:20
  • 7Sanders W S,Gibson L J.Materials Science and Engineering A[J],2003,347:70
  • 8Lim T J et al.Acta Materialia[J],2002,50:2867
  • 9China Aeronautical Materials Handbook Redaction Committee (中国航空材料手册编辑委员会).China Aeronautical Materials Handbook(中国航空材料手册)[M].Beijing:Standards Press of China,2002:565
  • 10Banhart J,Baumeister J.Journal of Materials Science[J],1998,33:1431

二级参考文献15

  • 1Evans A G, Hutchinson J W, Ashby M F. Multifunctionality of Cellular Metals Systems[J]. Progress in Materials Sciences,1999, 43:171.
  • 2Miyoshi T, Itoh M, Mukai T, Kanahashi H. Enhancement of Energy Absorption in a Closed-Cell Aluminum by the Modification of Cellular Structure[J]. Scripta Materialia, 1999, 41:1 055.
  • 3Deshpande V S, Fleck N A. High Strain Rate Compressive Behavior of Aluminum Alloy Foams[J]. International Journal of Impact Engineering, 2000, 24:277.
  • 4Mukai T, Kanahashi H, Yamada Y. Dynamic Compressive Behavior of an Ultra-Lightweight Magnesium Foam[J].Scripta Materialia, 1999, 41: 365.
  • 5Feng Y, Zhe Z G. Dynamic Compressive Behavior of Aluminum Alloy Foams[J]. Journal of Materials Science Letters,2001, 20:1 667.
  • 6Ashby M F, Medalist R F M. The Mechanical Properties of Cellular Solids[J]. Metallurgical Transactions, 1983, 14A:1 755.
  • 7Paul A, Ramamurty U. Strain Rate Sensitivity of a ClosedCell Aluminum Foam[J]. Materials Science and Engineering,2000, A281: 1.
  • 8Klintworth J W, Stronge W J. Elastic-Plastic Yield Limits and Deformation Laws for Transversely Crushed Honeycombs[J].International Journal of Mechanical Science, 1988, 30:273.
  • 9Philipse A P, Schram H L. Non-Darcian Airflow through Ceramic Foams[J]. Journal of American Ceramic Society,1991, 74:728.
  • 10Gibson L J, Ashby M F. Cellular Solids: Structure andProperties[M]. Cambridge: Cambridge University Press, 1997.

共引文献22

同被引文献66

引证文献3

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部