聚甲基苯基硅氧烷微球对聚碳酸酯性能的影响 被引量:5

Effect of Poly(methyl phenyl silsesquioxane) Microspheres on Properties of Polycarbonate
下载PDF
导出
摘要 研究了不同含量聚甲基苯基硅氧烷微球(PMPSQ)对聚碳酸酯(PC)阻燃性能、加工性能和力学性能等的影响。结果表明,随着 PMPSQ 含量的增加,冲击强度呈先上升后下降的趋势,PMPSQ 含量为5%时,冲击强度达到最大值,较空白 PC 提高了71.5%。PC 的阻燃性能随 PMPSQ 含量的增加而升高,当 PMPSQ 含量为5 %时,氧指数达到32.1%,较空白 PC 提高了23.0%。随着 PMPSO 含量的增加,PC 的玻璃化转变温度(T_g)逐渐下降,PMPSQ 含量为5%时,PC 的 T_g 从空白时的144.5℃降低至139.1℃。流变学分析表明,PMPSO 的加入可以有效降低 PC 的表观黏度,改善材料的加工性能。 The effect of poly(methyl phenyl silsesquioxane) (PMPSQ) on flame retardant, rheological, thermal and mechanical properties of polycarbonate (PC) was investigated. As the content of PMPSQ increased from 0 to 5 %, the impact strength of PC increased by 71.5 % and the LOI value increased by 23 %. Further increasing the content of PMPSQ, no additional improvement was observed. The inclusion of PMPSQ reduced the glass transition temperature(Tg) of PC, PMPSQ of 5 % caused Tg of PC decreased from 144.5 ℃ to 139.1 ℃. PMPSQ also resulted in reduction of the apparent viscosity of PC and thus enhanced its processability.
作者 王江波 辛忠
出处 《中国塑料》 CAS CSCD 北大核心 2008年第1期25-28,共4页 China Plastics
关键词 聚甲基苯基硅氧烷 聚碳酸酯 阻燃 加工性能 力学性能 poly(methyl phenyl silsesquioxane) polycarbonate flame retardancy processability mechanical property
  • 相关文献

参考文献5

二级参考文献34

  • 1廖兵,陈鸣才,黄玉惠,薛巍,徐丹宇.聚碳酸酯/ABS共混物的阻燃化研究[J].高分子材料科学与工程,1994,10(3):89-93. 被引量:10
  • 2Foti S, Giuffrida M, Manavigna P, et al. J. Polym.Sci. Polym. Chem. Ed., 1983, 21: 1567.
  • 3Montaudo G, Puglisi C. in Developments in Polymer Degradation Vol. 7 ed. Grassie N. Elsevire Applied Science, London, 1987: 35.
  • 4McNeill I C, Rineon A. Poly. Deg. and Stab., 1991,3:163-180.
  • 5Lee L H..I. Polym. Sci., 1964, 2:2859.
  • 6Davis A, Golden J H. J. Macromol. Sci. Rev. Macromol. Chem. 2968, C3: 49.
  • 7Mori H,Boker A,Krausch G,et al.Macromolecules,2001,34:6871.
  • 8Khan M,Huck W T S.Macromolecules,2003,36:5088.
  • 9Mulkern T J,Tan N C B.Polymer,2000,41:3193.
  • 10Nunez C M,Chiou B S,Andrady A L,et al.Macromolecules,2000,33:1720.

共引文献94

同被引文献510

引证文献5

二级引证文献17

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部