The La-Zn substituted SrM-type ferrites with the composition of Sr1-xLaxFe12-xZnxO19 （x=0-0.4） were prepared by self-propagating high-temperature synthesis （SHS）. The single SrM phase was detected by XRD in the as-received samples by controlling the Fe contents in the reagents. The substitution of La^3＋and Zn^2＋ obviously increased the magnetic properties of the as-prepared samples. The maximum improvements of Br, Hcb and （BH）m were 14.4%, 15.3% and 30.7%, respectively compared with that of the samples without La-Zn substitution. Microstructure observation by SEM showed that the SHS method benefited forming the better particle features and achieving the higher Hcj in comparison with the traditional firing method.
The La-Zn substituted SrM-type ferrites with the composition of Sr1-xLaxFe12-xZnxO19 （x=0-0.4） were prepared by self-propagating high-temperature synthesis （SHS）. The single SrM phase was detected by XRD in the as-received samples by controlling the Fe contents in the reagents. The substitution of La^3＋and Zn^2＋ obviously increased the magnetic properties of the as-prepared samples. The maximum improvements of Br, Hcb and （BH）m were 14.4%, 15.3% and 30.7%, respectively compared with that of the samples without La-Zn substitution. Microstructure observation by SEM showed that the SHS method benefited forming the better particle features and achieving the higher Hcj in comparison with the traditional firing method.
基金
Project supported by the Key Project for Science and Technology of Zhejiang Province