三维针刺C/SiC复合材料的结构特征和力学性能(英文) 被引量:8

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THREE-DIMENSIONAL NEEDLED C/SiC COMPOSITE
下载PDF
导出
摘要 采用化学气相渗透法制备了在厚度方向上具有纤维增强的三维针刺碳纤维增强碳化硅(C/SiC)陶瓷基复合材料,复合材料的密度和气孔率分别为2.15g/cm^3和16%。三维针刺C/SiC复合材料中的针刺纤维将各层紧密结合在一起,其层间抗剪切强度显著提高,为95MPa,比二维碳布叠层C/SiC复合材料的剪切强度(35MPa)高171.4%。三维针刺C/SiC复合材料的拉伸强度和弯曲强度分别为159MPa和350MPa,断裂模式为非脆性断裂,包括:裂纹扩展、偏转,碳纤维的拉伸断裂和逐步拔出。 A three-dimensional needled carbon fiber reinforced silicon carbide(3D needled C/SiC)ceramic matrix composite in the through-the-thickness direction was fabricated by the chemical vapor infiltration process.The resulting composite has a bulk density of 2.15 g/cma^3 and an open porosity of 16%.The adjacent layers for thickness direction in the 3D needled C/SiC composite are interlinked perfectly together by needling fibers and this greatly improves the interlaminar shear strength of the composite.The interlaminat shear strength of the 3D needled C/SiC composite is 95 MPa(improved 171.4% compared with 2D C/SiC composite,35 MPa), and the tensile strength and flexural strength of the 3D needled C/SiC composite are 159 MPa and 350 MPa,respectively.The composite exhibits a non-brittle failure behavior including propagation and deflection of cracks,fracture and pullout of fibers.
机构地区 西北工业大学
出处 《硅酸盐学报》 EI CAS CSCD 北大核心 2008年第2期144-149,共6页 Journal of The Chinese Ceramic Society
基金 国家自然科学基金(50672076)资助项目。
关键词 三维针刺 碳/碳化硅复合材料 结构特征 力学性能 three dimensional needled carbon fiber reinforced silicon carbide composites microstructure mechanical property
  • 相关文献

参考文献3

二级参考文献12

  • 1赵根祥,金允正,王健.硝酸法PAN基预氧丝在碳化期间分子结构的变化[J].高分子材料科学与工程,1995,11(1):46-49. 被引量:6
  • 2贺福 王茂章.炭纤维及其复合材料[M].北京:科学出版社,1997.9.
  • 3苏君明.碳化硅基热结构复合材料推力室的研制与应用前景.1996年联合推进会议文集[M].南宁,1996.210-214.
  • 4苏君明,1996年联合推进会议文集,1996年,210页
  • 5Blazewicz S. Carbon fibers from treated PAN precursor [ J ]. Carbon,1989, 27(6) :777 -783
  • 6Miller L M, Tague T J. Development and biomedical applications of fluorescence assisted synchrotron infrared micro-spectroscopy[J]. Vibrational Spectroscopy,2002, 28( 1 ) : 159 - 165
  • 7Zhu Y, Wilding M A, Mukhopadhyay S K. Estimation, using infrared spectroscopy, of the cyclization of poly (acrylonitrile) during the stabilization stage of carbon fiber production [ J ] .J Mater Sci ,1996, 31 (14) :3831 -3837
  • 8Zbinden R. Infrared spectroscopy of high polymers [ M ]. New York: Academic Press,1964. 213
  • 9Grassie N, McGuchan R. Pyrolysis of polyacrylonitrile and related polymers-Ⅱ, the effect of sample preparation on the thermal behavior of polyacrylonitrile [ J]. Eur Polym J, 1971, 7 (8) : 1091 -1104
  • 10Fochler HS, Mooney JR, Ball LE, et al. Infrared and NMR spectroscopic studies of the thermal degradation of polyacrylonitrile[ J].Spectrochim Acta,1985, 41A(1 -2) : 271 -278

共引文献27

同被引文献136

引证文献8

二级引证文献53

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部