摘要
采用脉冲激光沉积(PLD)方法在MgO/TiN/Si(100)衬底上,生长不同In掺杂量的SrIn_xTi_(1-x)O_3(x=0、0.1、0.2)薄膜,研究In掺杂及本征SrTiO_3(STO)缓冲层对薄膜结晶性能、表面形貌、生长模式及紫外拉曼光谱特性的影响.结果表明,In掺杂导致薄膜结晶度降低,通过引入本征STO缓冲层可有效提高In掺杂STO薄膜的结晶度,增强薄膜的(200)择优取向性.然而随In掺杂量的增加,薄膜表面平均粗糙度增大;生长模式由层状生长转变为岛状-层状复合模式;拉曼一次声子振动模式峰强逐渐增强,说明薄膜的晶体对称性降低.
Undoped and In-doped SrTiO3（STO） films were grown on MgO/TiN/Si（100） substrates by pulsed laser deposition（PLD）. The growth mechanism, crystallinity, surface morphology, and UV- Raman spectra of the films were studied. Results indicate that undoped STO films show high quality crystalline structure with highly （200） orientation. With Indium doping, the crystallinity of the STO film deteriorate, the first order Raman peaks increase indicating the breaking of crystal symmetry, and the film growth mode change from the layer-by-layer mode to island-layer mixed one, resulting in the roughening of the film surface. Furthermore, the crystallinity and （200） orientation of In-doped STO film can be enhanced significantly by introducing an undoped STO buffer layer.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2008年第3期531-534,共4页
Journal of Inorganic Materials
基金
国家重点基础研究发展计划项目(2002CB613306)
国家自然科学基金(90401010)