Lead-free piezoelectric ceramics （Na0.53K0.422Li0.048 ） （Nb0.89Sb0.06 Ta0.05 ）03 （NKLNST） ＋ x tool SrCO3 are prepared by conventional solid state sintering method. The specimens with pure perovskite structure show tetragonal phase at x 〈 0.01, and become pseudo-cubic phase at x 〉 0.02. A lattice parameter discontinuity is found in the specimens with 0.004 〈 x 〈 0.0075, along with a great improvement in piezoactivity. The 0.004 mol SrCO3 added NKLNST ceramics possesses outstanding performances of kp = 0.53, kt = 0.26, and d33=309 pC/N. Moreover, the Sr^2＋ modification inhibits the gra/n growth, decreases the Curie temperature, and induces a diffuse phase transition.
Lead-free piezoelectric ceramics （Na0.53K0.422Li0.048 ） （Nb0.89Sb0.06 Ta0.05 ）03 （NKLNST） ＋ x tool SrCO3 are prepared by conventional solid state sintering method. The specimens with pure perovskite structure show tetragonal phase at x 〈 0.01, and become pseudo-cubic phase at x 〉 0.02. A lattice parameter discontinuity is found in the specimens with 0.004 〈 x 〈 0.0075, along with a great improvement in piezoactivity. The 0.004 mol SrCO3 added NKLNST ceramics possesses outstanding performances of kp = 0.53, kt = 0.26, and d33=309 pC/N. Moreover, the Sr^2＋ modification inhibits the gra/n growth, decreases the Curie temperature, and induces a diffuse phase transition.
基金
Supported by the National Natural Science Foundation of China under Grant No 50572056, and Research Fund for the Doctoral Programme of High Education of China under Grant No 20070422059.