摘要
研究了预变形和热循环对Ti50.8Ni49.2及加入Fe和Nb后合金环的双程记忆应变影响。结果表明：在马氏体状态进行10.4%-13.8%的预变形,TiNi合金环随循环次数增加,双程记忆应变增大,在13.8%预变形和4次循环得到4.15%最大值;加入Fe和Nb后,在10.71%-15.18%的变形范围,合金环的双程记忆应变先增后降,其最大值分别为3.14%和2.56%。在变形量和循环次数相同时,TiNi合金环的记忆应变最高,当变形量和循环次数超过12.50%和2以后,TiNiFe合金环的双程记忆应变快速上升,其双程记忆应变超过TiNiNb合金环的。
The influence of pre-strains and number of thermal cycling on the two-way shape memory strains of TiNi, TiNiFe and TiNiNb alloy rings were investigated to provide theoretical basis for their applications in engineering. The results indicate that the two-way memory strains of TiNi alloy rings deformed at temperature less than Mf point increase with the increase of thermal cycling number within the range of 10.4% - 13.8% pre-strains. The maximum two-way memory strain of 4.15% is obtained at pre-strain of 13.8% and thermal cycling number up to 4. And when Fe or Nb atoms are added to TiNi alloys, the two-way memory strains of alloy rings first increase and then decrease at the ranges of 10. 71% - 15.18% pre-strains, their maximums are 3.14% and 2.56% , respectively. At the same prestrain and thermal cycling number, the two-way memory strains of TiNi alloy rings are the greatest,after pre-strain and cycling number are more than 12.50% and 2, the two-way memory strains of TiNiFe rings rapidly rise and are greater than that of TiNiNb alloy rings.
出处
《航空材料学报》
EI
CAS
CSCD
2008年第3期12-15,共4页
Journal of Aeronautical Materials
基金
高性能燃料及材料国防科技重点实验室资助项目(51481130101ZK0601)