A New Model of the Fatigue Life Curve of Materials
下载PDF
导出
摘要 分析了材料疲劳寿命曲线在三个阶段内的变化特性,提出了一个描述材料全寿命区域内疲劳寿命曲线的三参数模型。该模型中的三个参数分别反映了材料的疲劳极限、韧性以及特征疲劳寿命,同时给出了求解这些参数的方法。通过对载荷的量纲一化处理,该模型可以描述材料的应力-寿命曲线和应变-寿命曲线。对金属材料和复合材料的19条应力/应变-寿命曲线进行了统计分析,结果表明该模型可以描述材料的全寿命曲线。 The characteristics of fatigue life curve of materials in three stages of fatigue life were analyzed and then a model with three parameters was presented to describe the fatigue life curve of materials in the whole region.Three parameters quantitatively describe the fatigue limit,the toughness and the characteristic fatigue life of material in the model and a convenient method to obtain the parameters was mentioned.The model can describe the strain-life curve as well as stress-life curve of materials by the normalized loading.Nineteen sets of experimental data of metals and composites were employed to verify the model,and the results show that the model is capable to describe the fatigue life curve of materials in whole region.
出处 《中国机械工程》 EI CAS CSCD 北大核心 2008年第13期1634-1637,共4页 China Mechanical Engineering
关键词 疲劳寿命 S-N曲线 ε-N曲线 疲劳极限 韧性 fatigue life S-N curve ε-N curve fatigue limit toughness
  • 相关文献

参考文献16

  • 1郑立春,姚卫星.疲劳裂纹形成寿命预测方法综述[J].力学与实践,1996,18(4):9-14. 被引量:14
  • 2翟洪军,姚卫星.纤维增强树脂基复合材料的疲劳剩余刚度研究进展[J].力学进展,2002,32(1):69-80. 被引量:32
  • 3Coffin L F. A Study of the Effects of Cyclic Thermal Stresses on a Ductile Metal[J]. Transactions of the American Society of Mechanical Engineers (ASME), 1954, 76: 931-950.
  • 4Manson S S. Behaviour of Materials Under Condition of Thermal Stress [R]. NACA TA- 2933, 1954.
  • 5Jaske C E, Feddersen C E, Davis K B, et al. Analysis of Fatigue, Fatigue Crack Propagation, and Fracture Data[R]. NASA CR--132332, 1973.
  • 6高镇同.航空金属材料疲劳性能手册[M].北京:北京航空材料研究所,1981..
  • 7吴学仁.飞机结构金属材料力学性能手册(第一卷)静强度·疲劳/耐久性[M].北京:航空工业出版社,1996.
  • 8Donaldson S L, Kim R Y. Life Prediction of Glass/ Vinylester and Glass/Polyester Composites under Fatigue Loading[C]//Proceedings of the 10th International Conference on Composite Materialsfatigue and Fracture. Cambridge: Woodhead Publishing Limited, 1995 : 557-584.
  • 9Hwang W B, Han K S. Fatigue of Composite Materials Damage Model and Life Prediction[C]// Composite Materials Fatigue and Fracture, Philadelphia:American Society for Testing and Materials(ASTM STP 1012), 1989:87-102.
  • 10Broutman L J, Sahu S. A New Theory to Predict Cumulative Fatigue Damage in Fiberglass Reinforced Plastics[C]//Composite Materials: Testing and Design(Second Conference), Philadelphia: American Society for Testing and Materials (ASTM STP497). 1972: 170-188.

二级参考文献14

  • 1茆会勇,蒋咏秋,叶林.复合材料层板损伤过程的刚度分析[J].复合材料学报,1996,13(2):124-130. 被引量:7
  • 2邓梁波,王德劭.复合材料叠层板横向开裂的研究[J].复合材料学报,1997,14(1):127-134. 被引量:2
  • 3韩京燮 黄云峰.复合材料疲劳寿命的预测[J].复合材料学报,1987,4(1):16-24.
  • 4蒋咏秋 中国机械工程学会 等.复合材料的刚度下降及寿命估算.第三届全国疲劳学术交流会论文集[M].北京:中国机械工程学会,1986.1-8.
  • 5王殿富 中国航空学会.复合材料层合板疲劳的刚度衰退模型.第五届全国疲劳学术会议论文集[M].北京:中国航空学会,1991.16-21.
  • 6冯培锋 中国航空学会.复合材料层合板疲劳刚度的试验检测.第五届全国疲劳学术会议论文集[M].北京:中国航空学会,1991.30-33.
  • 7郭卫国 中国航空学会.复合材料层合板在疲劳加载下的剩余刚度.第五届全国疲劳学术会议论文集[M].北京:中国航空学会,1991.26-29.
  • 8李海涛 中国航空学会.复合材料层合板疲劳寿命预测.第五届全国疲劳学术会议论文集[M].北京:中国航空学会,1991.22-25.
  • 9卫丰 中国金属学会.复合材料层合板的分层实验分析.第六届全国断裂学术会议论文集[M].北京:中国金属学会,1991.468-471.
  • 10蒋咏秋 中国航空学会.分层损伤导致层合复合材料刚度下降.全国复合材料学术会议文集[M].北京:中国航空学会,1988.450-456.

共引文献62

同被引文献238

引证文献18

二级引证文献93

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部