摘要
以介孔氧化硅空心球(HMSS)为载体,采用双溶剂法浸渍硝酸钴溶液制备了高分散度的钴催化剂,并表征了催化剂中Co3O4颗粒的负载情况和费托(F-T)反应性能.结果表明:Co3O4颗粒在介孔硅球孔道内形成100～200nm左右分散良好的簇团,将催化剂压碎和刻蚀后的透射电子显微镜(TEM)证实,这些簇团是由尺寸约为10～15nm大小均匀的Co3O4单分散颗粒组成,这些单分散颗粒锚定在介孔硅球孔道内,彼此之间被相邻孔壁隔开;催化剂中钴-硅作用很弱,在600K下即可被还原;F-T反应评价表明,所得产物保持了良好的烃分布,主要集中于C5～C18烃,选择性在60%左右,C5+选择性达到80%以上。
High dispersion CO3O4 nano-particles supported on hollow mesoporous silica spheres （HMSS） were prepared by a novel two-solvent method. The supported nano-particles had been characterized and its catalytic performance had been evaluated. The Co3O4 single clusters were 100-200 nm and dispersed equably in the pore channels. HRTEM and TEM results showed that these single clusters were composed by 10-15 nm mono-dispersed CO3O4 nano-particles, and these CO3O4 nano-particles were loaded in the pore channels of the HMMS and were divided by the pore walls with each other. XRD and Raman spectra proved that the Co species in the catalysts were Co3O4 phase. The interaction between Co atom and Si atom was negligible, indicating that there was almost no Co2SiO3 in the catalysts and thus the samples were easily to be reduced. The catalysts have good performance and hydrocarbon distribution which concentrated on C5-C18 in F-T synthesis, C5- content could be above 80%.
出处
《化学学报》
SCIE
CAS
CSCD
北大核心
2008年第16期1851-1856,共6页
Acta Chimica Sinica
关键词
中空球
双溶剂
F-T合成
hollow mesoporous silica spheres （HMSS）
two-solvent
Fischer-Tropsch synthesis