摘要
The antiwear and friction-reducing performances of sodium borate, potassium borate and lanthanum chloride in water were evaluated on a four-ball friction tester. The topographies, element distribution and chemical characteristics of the worn surfaces were investigated by scanning electron microscope （SEM）, energy dispersion of X-ray （EDX） and X-ray photoelectron spectroscope （XPS）. The results indicated that sodium borate, potassium borate and lanthanum chloride increased extreme pressure, antiwear and friction-reducing capacities of water to a certain extent, of which potassium borate was the best candidate. Combination of lanthanum chloride with sodium borate and po- tassium borate respectively further improved antiwear and friction-reducing capacities. Scratches of worn surfaces lubricated with water containing borates and lanthanum chloride were less severe than those lubricated with water containing borates alone. A tribochemical film mainly composed of oxides of lanthanum, boron and iron reduced friction and wear for water lubricant formulated with both borates and lanthanum chloride.
The antiwear and friction-reducing performances of sodium borate, potassium borate and lanthanum chloride in water were evaluated on a four-ball friction tester. The topographies, element distribution and chemical characteristics of the worn surfaces were investigated by scanning electron microscope （SEM）, energy dispersion of X-ray （EDX） and X-ray photoelectron spectroscope （XPS）. The results indicated that sodium borate, potassium borate and lanthanum chloride increased extreme pressure, antiwear and friction-reducing capacities of water to a certain extent, of which potassium borate was the best candidate. Combination of lanthanum chloride with sodium borate and po- tassium borate respectively further improved antiwear and friction-reducing capacities. Scratches of worn surfaces lubricated with water containing borates and lanthanum chloride were less severe than those lubricated with water containing borates alone. A tribochemical film mainly composed of oxides of lanthanum, boron and iron reduced friction and wear for water lubricant formulated with both borates and lanthanum chloride.
基金
the National Natural Science Foundation of China (50275147)
Program for New Century Excellent Talents in Chinese University (NCET-04-1002)
Program for Innovative Groups in Chongqing’s Higher Schools