银在硫化钠溶液中的变色行为 被引量:4

Tarnishing Behavior of Silver in Sodium Sulfide Solution
下载PDF
导出
摘要 为研究银在硫化钠溶液中的变色机理及表面粗糙度对银变色的影响,使用扫描电镜和X-射线光电子能谱对银在硫化钠溶液中形成的变色膜进行表面形貌观察和成分分析,并通过电化学极化曲线和电化学阻抗谱技术对变色过程进行表征。结果显示银变色表面由一层均匀多孔的微小硫化银颗粒覆盖,颜色变化是颗粒大小以及覆盖密度在宏观上的反映。银在硫化钠溶液中的变色过程为硫化银粒子的不断长大堆积过程。通过比较表面粗糙度不同对银变色的影响,发现1500^#。砂纸打磨样品表面变色程度最轻,抛光样品变色最重,150^#、400^#、800^#砂纸打磨表面变色程度相近,居于二者之间。 In order to find the mechanism of silver tarnishing in sodium sulfide solution and the impact of surface roughness on silver tarnishing, SEM and XPS were used to analyze the appearance and composition of tarnished surface formed in sodium sulfide solution. Besides, electrochemical polarization and EIS were used to analyze the process of tarnishing. The results showed that the tarnished surface is covered by a thin and porous film which is composed of tiny silver sulfide particles. The differences in particles diameter and coverage density result in the change of color. It was found that 1500^# finished surface tarnishes the least seriously, polished surface tarnishes the most seriously, and 150^# , 400^# , and 800^# finished surface tarnishes at the similar middle degree.
出处 《装备环境工程》 CAS 2008年第5期33-37,共5页 Equipment Environmental Engineering
关键词 变色 硫化钠溶液 表面粗糙度 silver tarnish sodium sulfide solution surface roughness
  • 相关文献

参考文献15

  • 1RICE D W, PETERSON P, RIGBY E B, et al. Atmospheric Corrosion of Copper and Silver [J]. J Electrochem Soc, 1981,128(2) :275--284.
  • 2FRANEY J P, KAMMLOTT G W, GRAEDEL T E. The Corrosion of Silver by Atmospheric Sulfurous Gases[J]. Corrosion Sience,1985,25(2):133--143.
  • 3KIM H. Corrosion Process of Silver in Environments Containing 0.1 ppm H2S and 1.2 ppm NO2[J]. Materials and Corrosion ,2003 ,54(4) :243--250.
  • 4REAGOR B T,SINCLAIR J D. Tarnishing of Silver by Sulfur Vapor: Film Characteristics and Humidity Effects[J]. J Electrochem Soc, 1981, 128 (3):701-- 705.
  • 5SINCLAIR J D. Tarnishing of Silver by Organic Sulfur Vapors:Rates and Film Characteristics[J]. J Electrochem. Soc,1982,129(1) :33--40.
  • 6EVESQUE Magali, KEDDAM Michel, TAKENOUTI Hisasi. The Formation of Self assembling Membrane of Hexaclecane-thiol on Silver to Prevent the Tarnishing[J]. Electrochimica Acta, 2004,49(17--18) :2937 --2943.
  • 7BURLEIGH T, GU D, DONAHEY Y G,et al. Tarnish Protection of Silver using a Hexadecanethiol Selfassembled Monolayer and Descriptions of Accelerated Tarnish Tests [J]. Corrosion Engineering Section, 2001,58 (12):1066 -- 1074.
  • 8张东曙,蔡兰坤,祝鸿范,周浩.复配缓蚀剂防银变色协同效应的研究[J].材料保护,2002,35(2):26-27. 被引量:5
  • 9张东曙,蔡兰坤,祝鸿范,周浩.银表面防变色膜PMM性能研究[J].中国腐蚀与防护学报,2002,22(5):304-307. 被引量:11
  • 10伯恩斯[美].颜色技术原理[M].北京:化学工业出版社,2002:12i3.

二级参考文献15

共引文献64

同被引文献26

引证文献4

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部