用DSC研究了PA1010/6共聚物初生态及次生态样品的熔融行为,发现初生态样品的高温熔融峰(T1)和低温熔融峰(T2)对组成有不同的依赖关系;首次发现PA1010/6共聚物次生态的冷结晶现象,并讨论了冷结晶温度(TC)、冷结晶时间(tc)与组成的关系.
Thermal decomposition of ammonium molybdate is studied by thermal gravimetric analysis(TG) and differential thermal analysis(DTA) The results indicate that ammonium molybdate is thermally decomposed in three steps: in the temperature range of 353~473K,the crystal water was mainly removed ,and the structure of ammonium molybdate is remained, in the temperature range of 473~573K,the crystal water could be completely removed while a fraction of the ammonium ions were lost to produce one kind of metastable molybdena species, at temperature above 573K, the residual ammonium ions could be completely removed, therefore rearrangement of the molybdena subsequently occurred to form the bulk phase of MoO 3
出处
《郑州大学学报(自然科学版)》
1997年第3期67-70,73,共5页
Journal of Zhengzhou University (Natural Science)
基金
河南省优秀中青年科技人才专项基金
中科院长春应化所高分子物理开放实验室基金
关键词
PA1010/6共聚物
熔融
冷结晶
初生态
次生态
thermal gravimetric analysis (TG)
differential thermal (DTA)
ammonium molybdate
thermal decomposition