有序介孔C/NiO复合材料的合成及其电化学性能 被引量:10

Preparation and Electrochemical Properties of Ordered Mesoporous C/NiO Composites
下载PDF
导出
摘要 以嵌段共聚物F127(Mw=12600,PEO106PPO70PEO106)为模板剂,Ni(Ac)2·4H2O为Ni源,低分子量的酚醛树酯为碳源,通过溶胶-凝胶三元共组装方法合成高度有序介孔C/NiO复合材料.对样品进行X射线衍射(XRD)、透射电子显微镜(TEM)、N2吸脱附等结构表征及循环伏安(CV)等电化学性能测试.结果显示,NiO晶体和碳组成了C/NiO复合材料的基本骨架,该复合材料具有高度有序的介孔结构.NiO晶体的存在极大地提高了复合材料的电化学性能,当C/NiO达到4∶1(苯酚与Ni(Ac)2·4H2O的摩尔比)时复合材料的比电容达到444.1F·g-1,而有序的介孔结构并没有被破坏,使得该材料具有较好的应用前景. Highly ordered mesoporous C/NiO composites were synthesized via the sol-gel process using an amphiphilic triblock copolymer F127 (Mw=12600, PEO106,PPO70PEO106) as a template, Ni(OAc)2 as nickel source and resols as an organic precursor. X-ray diffraction (XRD), transmission electron microscopy (TEM), and nitrogen adsorption were used to characterize the structure. Cyclic voltammetry (CV) was used to test the electrochemical properties of the samples. The results showed that the backbone of the mesoporous structures consisted of NiO nanocrystallites and carbon. The C/NiO composites have a highly ordered mesostructure. The presence of NiO nanocrystallites was expected to improve the capacitance properties of the composite. At a C/NiO ratio of 4:1 (molar ratio of phenol to nickel acetate) the composite had a large specific capacitance of 444.1 F·g^-1 and the ordered mesostructure remained intact. Ordered mesoporous C/ NiO composites thus are promising for applications,
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 2008年第12期2314-2320,共7页 Acta Physico-Chimica Sinica
基金 江苏省高新技术(BG2005009) 航空科学基金(2007ZF52061)资助项目
关键词 有序 介孔C/NiO 溶胶-凝胶法 比电容 Ordered Mesoporous C/NiO Sol-gel method Specific capacitance
  • 相关文献

参考文献22

  • 1Ryoo, R.; Joo, S. H.; Kruk, M.; Jaroniec, M. Adv. Mater., 2001, 13:677
  • 2Meng, Y.; Gu, D.; Zhang, F. Q.; Shi, Y. F.; Yang, H. F.; Li, Z.; Yu, C. Z.; Tu, B.; Zhao, D. Y. Angew. Chem. Int. Edit., 2005, 44:7053
  • 3Nam, K. W.; Kim, K. B. J. Electrochem. Soc., 2002, 149(3): A346
  • 4程杰,曹高萍,杨裕生.Ni(OH)2干凝胶超级电容器研究.第五届亚洲电化学会议,上海复旦大学,2005
  • 5Li, H. F.; Zhu, S. M.; Xi, H. A. Micropor. Mesopor. Mater., 2006, 89:196
  • 6Xing, W.; Li, F.; Yan, Z. F.; Lu, G. Q. J. Power Sources, 2004, 134:324
  • 7Zhu, S. M.; Zhou, H. S.; Hibino, M.; Honma, I.; Ichihara, M. Adv. Funct. Mater., 2005, 15:381
  • 8Yao, W. L.; Wang, J. L.; Yang, J.; Du, G. D. J. Power Sources, 2008, 176:369
  • 9Zheng, Y. Z.; Zhang, M. L.; Gao, P. Mater Res. Bull., 2007, 42: 1740
  • 10张传香,何建平,周建华,赵桂网,陈秀,王涛.有序介孔碳CMK-3微波负载NiO及其电容性能研究[J].化学学报,2008,66(6):603-608. 被引量:7

二级参考文献25

  • 1Frackowiak, E. Phys. Chem. Chem. Phys. 2007, 9, 1774.
  • 2Tamai, H.; Kunihiro, M. J. Mater. Sci. 2005, 40, 3703.
  • 3Ryoo, R.; Joo, S. H.; Jun, S. J. Phys. Chem. B 1999, 103, 7743.
  • 4Ryoo, R.; Joo, S. H.; Kruk, M.; Jaroniec, M. Adv. Mater. 2001, 13, 677.
  • 5Joo, S. H.; Choi, S. J.; Oh, I; Kwak, J.; Liu, Z.; Terasaki, O.;Ryoo, R. Nature 2001, 412, 169.
  • 6Lee, J.; Yoon, S.; Hyeon, T.; Oh, S. M.; Kim, K. B. Chem. Commun. 1999, 2177.
  • 7Lee, J. S.; Joo, S. H.: Ryoo, R. J. Am. Chem. Soc. 2002, 124, 1156.
  • 8Huwe, H.; Froba, M. Carbon 2007, 45, 304.
  • 9Li, H. F.; Zhu, S. M.; Wang, R. D. Microporous Mesoporous Mater. 2006, 89, 196.
  • 10Xing, W.; Li, F.; Yan, Z. F.; Lua, G. Q. J. Power Sources 200,:1, 134, 324.

共引文献6

同被引文献178

引证文献10

二级引证文献69

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部