Effect of Gd content on microstructure and mechanical properties of Mg-Y-RE-Zr alloys 被引量:7

Effect of Gd content on microstructure and mechanical properties of Mg-Y-RE-Zr alloys
下载PDF
导出
摘要 Four kinds of Mg-Y-RE-Zr alloys with different Gd contents were prepared,and the effect of Gd content on microstructure and mechanical properties of the alloys was researched.Based on the experimental investigation,the compounds at the grain boundaries are mainly Mg_(24)Y_5,Mg_(41)Nd_5,and Mg_5Gd phases.The average grain size of as-cast alloys is 50-60μm.After T4(535℃, 24 h)treatment,Mg_5Gd phases mostly decompose and dissolve into the matrix,and the disperse spotted phases are mainly Mg_(24)Y_5 and Mg_(41)Nd_5 phases.After extruding and ageing(250℃,5 h),the grain size is refined and some grains abnormally grow up to about 40μm.With Gd content increasing,the ultimate tensile strength,yield strength of as-cast alloys and the extruded bars after ageing are improved,but the elongation is decreased. Four kinds of Mg-Y-RE-Zr alloys with different Gd contents were prepared, and the effect of Gd content on microstructure and mechanical properties of the alloys was researched. Based on the experimental investigation, the compounds at the grain boundaries are mainly Mg24Y5, Mg41Nd5, and Mg5Gd phases. The average grain size of as-cast alloys is 50-60 um. After T4 (535℃, 24 h)treatment, Mg5Gd phases mostly decompose and dissolve into the matrix, and the disperse spotted phases are mainly Mg24Y5 and Mg41Nd5 phases. After extruding and ageing (250 ℃, 5 h), the grain size is refined and some grains abnormally grow up to about 40 um. With Gd content increasing, the ultimate tensile strength, yield strength of as-cast alloys and the extruded bars after ageing are improved, but the elongation is decreased.
出处 《中国有色金属学会会刊:英文版》 CSCD 2008年第A01期12-16,共5页 Transactions of Nonferrous Metals Society of China
基金 Project(2007CB613705)supported by the National Basic Research Program of China Project(2006BAE04B01)supported by the NationalScience and Technique Support Program during the 11th Five-Year Period of China.
关键词 挤压成型 合金 微观结构 镁合金 钆合金 Mg-Y-RE-Zr alloy Gd microstructure mechanical properties
  • 相关文献

参考文献2

二级参考文献18

  • 1彭卓凯,张新明,陈健美,肖阳,蒋浩,邓桢桢.Mn,Zr对Mg-Gd-Y合金组织与力学性能的影响[J].中国有色金属学报,2005,15(6):917-922. 被引量:50
  • 2Mordike B L.Creep-resistant magnesium alloys[J].Mater Sci Eng A,2002,A324:103-112.
  • 3Maruyama K,Suzuki M,Sato H.Creep strength of Magnesium-based alloys[J].Metall Mater Trans A,2002,A33(3):875-882.
  • 4Anyanwu I A,Kamado S,Kojima Y.Aging characteristics and high temperature tensile properties of Mg-Gd-Y-Zr alloys[J].Mater Trans,2001,42(7):1206-1211.
  • 5Anyanwu I A,Kamado S,Kojima Y.Creep properties of Mg-Gd-Y-Zr alloys[J].Mater Trans,2001,42(7):1212-1218.
  • 6Shigeru I,Yuji N,Shigeharu K,et al.Age hardening characteristics and high temperature tensile properties of Mg-Gd and Mg-Dy alloys[J].Journal of Japan Institute of Light Metals,1994,44(1):3-8.
  • 7Shigeharu K,Yutaka K,Yoshitada H.High temperature deformation characteristics and forgeability of Mg-Heavy rare earth element-Zr alloys[J].Journal of Japan Institute of Light Metals,1998,48(4):168-173.
  • 8Kawabata T,Matsuda K,Kamado S,et al.HRTEM observation of the precipitates in Mg-Gd-Y-Zr alloy[J].Materials Science Forum,2003,419-422:303-306.
  • 9Honma T,Ohkubo T,Hono K,et al.Chemistry of nanoscale precipitates in Mg-2.1Gd-0.6Y-0.2Zr(%)alloy investigated by the atom probe technique[J].Mater Sci Eng A,2005,A395:301-306.
  • 10Peng Z K,Zheng X M,Chen J M,et al.Grain refining mechanism in Mg-9Gd-4Y alloys by Zirconium[J].Mater Sci Technol,2005,21(6):722-726.

共引文献28

同被引文献74

引证文献7

二级引证文献31

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部