Sn对TiCp/Fe复合材料组织与性能影响的研究

Influence of Stannum on Microstructure and Properties of TiC_p/Fe Composite
下载PDF
导出
摘要 采用原位白生合成法制备了TiCp/Fe复合材料。借助光学显微镜及扫描电镜等,研究了Sn对TiCp/Fe复合材料组织和性能的影响。结果表明,随Sn含量增加,组织中片状石墨有害相得到有效抑制,且TiCp/Fe复合材料硬度、抗拉强度和冲击韧性也得到明显提高。分析得出制备TiCp/Fe复合材料的最佳Sn成分为0.1%~0.15%。 TiC reinforced Fe matrix composites have been prepared by in-situ reaction synthesis process. The influences of stannum on the microstructure and properties of TiCp/Fe composite have been investigated by using optical microscopy and .SEM. Results show that with the increasing of stannum, not only the flake graphite is suppressed effectively, but also the hardness, tensile strength and impact toughness of the TiCp/Fe composite were improved obviously. Further analysis shows that 0.1%-0.15% Sn is the suitable content.
出处 《铸造》 CAS CSCD 北大核心 2009年第1期36-38,共3页 Foundry
基金 广西科学基金资助项目(桂科字0339002)
关键词 原位自生 TICP/FE复合材料 硬度 抗拉强度 冲击韧性 in-situ reaction TiCp/Fe composite hardness tensile strength impact toughness
  • 相关文献

参考文献2

二级参考文献11

共引文献59

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部