实验测试了纯离子液体BMIMPF6、BMIMPF6-乙腈、BMIMPF6-碳酸丙二醇脂混合体系的粘度和电导率。应用循环伏安法在玻碳电极表面合成了聚噻吩,并测试了聚噻吩修饰电极在上述各溶液中的电化学行为。结果表明,聚噻吩在纯离子液体中的惨杂电量较小,电化学反应的可逆性较差。聚噻吩的氧化参杂电量与混合溶液的电导率呈明显的线性关系,当离子液体的体积含量为25%时,溶液的电导率达到最大,同时聚噻吩惨杂电量也达到最大,反应可逆也得到了明显的改善。
The polythiophene film was prepared by electropolymerization at glass carbon（ GC ）electrode using cyclic voltammetry and the electrochemical behavior of polythiophene film in neat ionic liquid BMIMPF6 . BMIMPF6/acetonitrile （ACN）and BMIMPF6/ propylene carbonate（PC） mixtures was measured. The viscosities and conductivities of the mixtures were also investigated. Results showed that the electrochemical capacity of polythiophene linearly increased with the increasing of the solution conductivity. The maximum electrochemical capacity of polythiophene film were observed in BMIMPF6/ACN（25/75v/v ）mixture ,which is about 7 times greater than that observed in neat BMIMPF6.
出处
《化学研究与应用》
CAS
CSCD
北大核心
2009年第2期175-179,共5页
Chemical Research and Application
基金
国家自然科学基金(20503016)资助
上海市科委启明星基金(07QA14044)资助
湖南大学生物传感与计量学国家重点实验室开放基金资助
关键词
离子液体
聚噻吩
导电率
电容器
ionic liquid
polythiophene
conductivity
electrochemical capability