Deformation behavior and dynamic recrystallization of Mg-Y-Nd-Gd-Zr alloy 被引量:7

Deformation behavior and dynamic recrystallization of Mg-Y-Nd-Gd-Zr alloy
下载PDF
导出
摘要 The characteristics of dynamic recrystallization (DRX) in Mg-Y-Nd-Gd-Zr-RE magnesium alloy were investigated by compression tests at temperatures between 523 and 723 K and at strain rates ranging from 0.002 to 1 s^-1 with maximum strain of 0.693. The strainhardening rate can be obtained from true stress-true strain curves, plots of θ-σ, -(δθ/δσ-)-a and lnθ-σ in different compression conditions were obtained by further study. The critical condition of the onset of DRX process was determined as ((δ/δσ( δθ/δσ))=0. In the range of the above deformation temperature and strain rate, the ratio of critical stress (σc) to peak stress (σm) and critical strain (εc) to the peak strain (εm) stood at σc/σm=0.62-0.89 and εc/εm=0.11-0.37, respectively. DRX could be observed during hot detormation process, microstructure evolution of the magnesium alloy at different temperatures and strain rates were studied with the aid of optical microscope(OM), and the average recrystallized grain size was measured by means of intercepts on photomicrographs. It was shown that the average dynamically recrystallized grain size (drew) changed with different deformation parameters, the natural logarithm of the average recrystallized grain size varied linearly with the natural logarithm of Zener-Hollomon parameter; the peak stress changed with the average recrystallized grain size, and the natural logarithm of the average recrystallized grain size varied linearly with the natural logarithm of the peak stress. The characteristics of dynamic recrystallization (DRX) in Mg-Y-Nd-Gd-Zr-RE magnesium alloy were investigated by compression tests at temperatures between 523 and 723 K and at strain rates ranging from 0.002 to 1 s^-1 with maximum strain of 0.693. The strainhardening rate can be obtained from true stress-true strain curves, plots of θ-σ, -(δθ/δσ-)-a and lnθ-σ in different compression conditions were obtained by further study. The critical condition of the onset of DRX process was determined as ((δ/δσ( δθ/δσ))=0. In the range of the above deformation temperature and strain rate, the ratio of critical stress (σc) to peak stress (σm) and critical strain (εc) to the peak strain (εm) stood at σc/σm=0.62-0.89 and εc/εm=0.11-0.37, respectively. DRX could be observed during hot detormation process, microstructure evolution of the magnesium alloy at different temperatures and strain rates were studied with the aid of optical microscope(OM), and the average recrystallized grain size was measured by means of intercepts on photomicrographs. It was shown that the average dynamically recrystallized grain size (drew) changed with different deformation parameters, the natural logarithm of the average recrystallized grain size varied linearly with the natural logarithm of Zener-Hollomon parameter; the peak stress changed with the average recrystallized grain size, and the natural logarithm of the average recrystallized grain size varied linearly with the natural logarithm of the peak stress.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2008年第6期846-850,共5页 稀土学报(英文版)
基金 supported by the National "Eleventh Five-Year Plan" Key Technologies R&D Program (2006BAE04B01)
关键词 hot-compression dynamic recrystallization (DRX) strain-hardening rate average recrystallized grain size rare earths hot-compression dynamic recrystallization (DRX) strain-hardening rate average recrystallized grain size rare earths
  • 相关文献

参考文献2

二级参考文献33

  • 1郭强,张辉,陈振华,严红革,夏伟军,傅定发.AZ31镁合金的高温热压缩流变应力行为的研究[J].湘潭大学自然科学学报,2004,26(3):108-111. 被引量:20
  • 2[1]Westengen H K. Magnesium die casting: from ingots to automotive parts[J]. Light Metal Age, 2000, 58(3-4): 44-52.
  • 3[2]Dwain M, Magers A. Global review of magnesium parts in automobiles[J]. Light Metal Age, 1996, 54(9-10): 60-63.
  • 4[3]Luo A, Pekguleryuz M O. Review cast magnesium alloys for elevated temperature applications[J]. Journal of Materials Science, 1994, 29(20): 5259-5271.
  • 5[4]Avedesian M M, Baker H. ASM Specialty Handbook-Magnesium and Magnesium Alloys[M]. USA: ASM International, 1999: 1-30.
  • 6[5]Wiley J. Magnesium and its Alloys[M]. USA: Sons Inc, 1960: 177-180.
  • 7[6]Kubota K, Mabuchi M, Higashi K. Review processing and mechanical properties of fine-grained magnesium alloys[J]. Journal of Materials Science, 1999, 34(10): 4311-4320.
  • 8[7]Kojima Y. Platform science and technology for advanced magnesium alloys[J]. Materials Science Forum, 2000, 350-351: 3-18.
  • 9[8]Mabuch M, Nakamura M, Ameyama K. Superplastic behavior of magnesium alloy processed by ECAE[J]. Materials Science Forum, 1999, 304-306: 67-72.
  • 10[9]Watanabe H, Mukai T, Higashi K. Low temperature superplastic behavior in ZK60 magnesium alloy[J]. Materials Science Forum, 1999, 304-306: 303-308.

共引文献177

同被引文献105

引证文献7

二级引证文献36

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部