采用氧化物陶瓷工艺制备MnZn功率铁氧体,研究了不同Ta2O5含量对MnZn功率铁氧体微观结构和磁性能的影响.结果表明:少量Ta2O5的加入可以使铁氧体烧结样品的晶粒尺寸增大,气孔率下降,起始磁导率、饱和磁感应强度和电阻率升高,损耗降低.而加入过多的Ta2O5会导致异常晶粒长大,气孔率升高,起始磁导率、饱和磁感应强度和电阻率降低,损耗增大.当Ta2O5含量为0.04wt%时,铁氧体烧结样品的晶粒尺寸大小均匀,气孔率最低,起始磁导率、饱和磁感应强度和电阻率达到最大值,损耗最低.
MnZn ferrites with the chemical formula Mn0.68 Zn0.25 Fe2.07 O4 were prepared by conventional ceramic techniques. The influence of Ta2O5 addition on the microstructure and magnetic properties of MnZn ferrites was investigated. When the Ta2O5 addition is less than 0.04wt%, the grain size increases with the increase of Ta2O5 concentration, the initial permeability, saturation magnetic flux density and DC resistivity increase, the power losses and porosity decrease. However, excessive Ta2O5 addition （ 〉0.04wt% ） results in the exaggerated grain growth and porosity increase which make the initial permeability, saturation magnetic flux density and DC resistivity decrease, and the power losses increase. When the Ta2O5 addition is 0.04wt%, the initial permeability, saturation magnetic flux density and DC resistivity reach the maximum, the power losses and porosity reach the minimum.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2009年第2期379-382,共4页
Journal of Inorganic Materials
基金
四川省科技攻关项目(2006Z02-032)