JOB-9003炸药的载荷环境试验 被引量:5

Load Environmental Test of Explosive JOB-9003
下载PDF
导出
摘要 在5M Pa轴向压应力条件下,对JOB-9003炸药进行了温度循环试验,结果表明,试验后炸药性能发生了明显的变化。JOB-9003炸药在载荷环境和温度循环的共同作用下其径向尺寸增加,轴向尺寸减小,而且径向尺寸的增加量与轴向尺寸的减小量相当。与轴向尺寸相比,径向尺寸对样品体积的影响更大,试验后样品体积变大,密度降低,同时炸药的压缩强度、最大蠕变应变和压缩蠕变断裂时间出现了明显降低,而模量变化不明显。分析认为,JOB-9003炸药内部的微孔隙和微损伤在载荷环境试验下发生变化,从而使JOB-9003炸药的尺寸、密度和力学性能出现了上述变化规律。 The load environmental tests of 5 MPa axial compression stress have been applied to explosive JOB-9003 under the temperature circulation. The test data show that the properties of the explosive have changed obviously after the tests. Under the condition of load environmental and temperature circulation, the radial dimension of explosive JOB-9003 increases while the axial dimension decreases, The changes of the two dimension are proximite. Comparing to the axial dimension, the contribution of the radial dimension to the volume is greater. So the volume of the sample increase and the density reduce. In addition, the compressive strength, the maximum creep strain and the creep rupture time all reduce obviously. But the modulus keeps no changes. It is analyzed that, the changes of the dimension, density and mechanical properties are owing to the changes of the tiny cavities in explosive JOB 9003 in the load environmental tests.
出处 《火炸药学报》 EI CAS CSCD 北大核心 2009年第1期36-39,共4页 Chinese Journal of Explosives & Propellants
基金 中国工程物理研究院预先研究项目(426040401)
关键词 材料力学 JOB-9003炸药 载荷环境试验 力学性能 material science JOB-9003 explosive load environmental test mechanical property
  • 相关文献

参考文献12

二级参考文献37

  • 1田勇,张伟斌,郝莹,李敬民,温茂萍.炸药热冲击损伤破坏及超声波特性参量检测[J].火炸药学报,2000,23(4):13-15. 被引量:24
  • 2许光,吴承云,于荫林,秦亚萍,汪辉.混合炸药对温度渐变环境的适应性研究[J].火炸药,1997,20(1):15-19. 被引量:11
  • 3Goldrein H T,Rae P .J,Palmer J P,et al. Ageing effects on the mechanical properties of a polymer bonded explosive. Ageing studies and lifetime extension of materials[M]. Edited by Mallinson, Kluwer Academic/PlenumPublishers ,2001.
  • 4Sandusky H W, Bernerker R R. Influence of fresh damage on the shock reactivity and sensitivity of several energetic materials[ A]. Proceedings of 10th Symposium ( International) on Detonation [ C ], 1993. 490 - 498.
  • 5Yvonne M, Lanzerotti D,Pinto J. Fracture surface topography of TNT,composition B and Octol [ A ]. Proceedings of 10th Symposium (International) on Detonation [ C ],1993. 190 - 198.
  • 6UCRL-LR-13204. Enhanced Surveillance Program FY1998Accomplishments[R]. 1998.10.
  • 7Richter H P,Boyer LR,Graham K J,et al. Shock sensitivity of damaged energetic materials[A]. Proceedings of the 9th Symposium (International) on Detonation [ C ], 1989.1295 - 1300.
  • 8Demol G, Lambert P,Trumel H. A study of the microstructure of pressed TATB and its evolution after several kinds of solicitations [ A ]. 11 th International Detonation Symposium[ C] , 1998.
  • 9Bernecker R R, Clairmont A R Jr. Shock initiation studies of cast, damaged and granulated PBXs [ A ]. Proceedings of 10th Symposium ( International ) on Detonation [ C ],1993. 499 - 506.
  • 10Green E L,James E Lee. Energetic response of propellants to high velocity impact[ A]. Proceedings of 8th Symposium (International) on Detonation [ C ], 1985. 284 - 293.

共引文献63

同被引文献40

引证文献5

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部