Long-lasting SrAl2O4∶Eu, Dy phosphor was successfully prepared from a mesoporous precursor. The precursor was synthesized by templating method using nonionic Polyethylene Oxide (PEO) as surfactants, which was proved by TG-DTG, X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM) analysis. The analysis results indicated that regular cylindrical-to-hexagonal shaped pores with several nanometers were obtained. The structure and morphology of the SrAl2O4∶Eu, Dy phosphor by templating method was characterized by XRD and Scanning Electron Microscopy (SEM). The XRD results showed that a pure SrAl2O4 phase formed at 900 ℃ by templating method. The SEM morphologies of the obtained phosphors prepared by templating synthesis were uniform and porous multicrystalline with average diameter size of 5 μm. The broad-band UV-excited SrAl2O4∶Eu, Dy phosphor derived from a mosoporous precursor was observed at λmax=515 nm due to the transitions from the 4f65d1 to the 4f7 configurations of Eu2+ ion. The main excitation and emission intensity of the phosphor with this method were stronger than that obtained by solid state reaction method. And the obtained long-lasting phosphor with this method revealed a better afterglow compared to the phosphor prepared through solid state reaction method.
Long-lasting SrAl2O4∶Eu, Dy phosphor was successfully prepared from a mesoporous precursor. The precursor was synthesized by templating method using nonionic Polyethylene Oxide (PEO) as surfactants, which was proved by TG-DTG, X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM) analysis. The analysis results indicated that regular cylindrical-to-hexagonal shaped pores with several nanometers were obtained. The structure and morphology of the SrAl2O4∶Eu, Dy phosphor by templating method was characterized by XRD and Scanning Electron Microscopy (SEM). The XRD results showed that a pure SrAl2O4 phase formed at 900 ℃ by templating method. The SEM morphologies of the obtained phosphors prepared by templating synthesis were uniform and porous multicrystalline with average diameter size of 5 μm. The broad-band UV-excited SrAl2O4∶Eu, Dy phosphor derived from a mosoporous precursor was observed at λmax=515 nm due to the transitions from the 4f65d1 to the 4f7 configurations of Eu2+ ion. The main excitation and emission intensity of the phosphor with this method were stronger than that obtained by solid state reaction method. And the obtained long-lasting phosphor with this method revealed a better afterglow compared to the phosphor prepared through solid state reaction method.
基金
the National Natural Science Foundation of China (20376009)