Sn-Sb peritectic alloy was treated with 400 W, 600 W and 800 W ultrasonic, respectively, to study the effect of power ultrasonic on solidification microstructure. Results show that power ultrasonic can refine α phase and β phase of the alloy, as well as eliminate gravitational segregation. Moreover, 600 W ultrasonic demonstrated the best refining effect, not only homogenous and fine solidification microstructure can be obtained, the cubical β phase crystals can also be spheroidized.
Sn-Sb peritectic alloy was treated with 400 W, 600 W and 800 W ultrasonic, respectively, to study the effect of power ultrasonic on solidification microstructure. Results show that power ultrasonic can refine α phase and β phase of the alloy, as well as eliminate gravitational segregation. Moreover, 600 W ultrasonic demonstrated the best refining effect, not only homogenous and fine solidification microstructure can be obtained, the cubical β phase crystals can also be spheroidized.