SOLIDIFICATION AND MICROSEGREGATION BEHAVIORS OF NICKEL-BASE SINGLE CRYSTAL SUPERALLOY SOLIDIFIED AT MEDIUM COOLING RATE 被引量:1

SOLIDIFICATION AND MICROSEGREGATION BEHAVIORS OF NICKELBASE SINGLE CRYSTAL SUPERALLOY SOLIDIFIED AT MEDIUM COOLING RATE
下载PDF
导出
摘要 SOLIDIFICATIONANDMICROSEGREGATIONBEHAVIORSOFNICKELBASESINGLECRYSTALSUPERALLOYSOLIDIFIEDATMEDIUMCOOLINGRATE①DuWei,LiJianguoan... Single crystal blades have already been used in some advanced engines. An industrially valuable nickelbase single crystal superalloy CMSX2 was solidified at cooling rate from below 1 K/s to 20 K/s. Microstructure and microsegregation were investigated. The results showed that the dendritic arm spacing is highly refined at high cooling rate, the primary dendritic arm spacing can be 35 μm, just as 1/10 as that by conventional HRS processing. With the increase of cooling rate, the microsegregation increases and then decreases. In the superfine columnar dendrite, the γ′ precipitates are very fine; the amount of γ/γ′ eutectic is much fewer and its size is very small.
出处 《中国有色金属学会会刊:英文版》 CSCD 1998年第1期84-88,共5页 Transactions of Nonferrous Metals Society of China
关键词 SINGLE CRYSTAL SUPERALLOY COOLING RATE microstructure MICROSEGREGATION single crystal superalloy cooling rate microstructure microsegregation
  • 相关文献

同被引文献8

引证文献1

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部