Effect of Li and Ti additions on Lα(AI)+Mg2Si pseudobinary eutectic reaction in ternary Al-Mg-Si system has been investigated by thermoanalysis, directional solidification and metallographic techniques in this study. It has been found that Li addition causes decreasing of the volume fraction of Mg2Si, while a little amount of Ti causes to increasing, which is of a great importance to the adjustment of phase constitution and alloy properties. Doping components have little influence on the eutectic temperature.
Effect of Li and Ti additions on Lα(AI)+Mg2Si pseudobinary eutectic reaction in ternary Al-Mg-Si system has been investigated by thermoanalysis, directional solidification and metallographic techniques in this study. It has been found that Li addition causes decreasing of the volume fraction of Mg2Si, while a little amount of Ti causes to increasing, which is of a great importance to the adjustment of phase constitution and alloy properties. Doping components have little influence on the eutectic temperature.