The grain boundary internal friction(GBIF)in Fe-P and Fe-P-La alloys containing trace Cu has been studied.It is found that an addition of 0.584—0.722 wt-% La obviously reduces the IF,shifts grain boundary peaks towards higher temperatures,and produces a small addi- tional peak at even higher temperature.The mechanism of GBIF is explained as the movement of defects of atomic size,namely point defects,at gram boundaries and/or their clusters un- der stress.
The grain boundary internal friction(GBIF)in Fe-P and Fe-P-La alloys containing trace Cu has been studied.It is found that an addition of 0.584—0.722 wt-% La obviously reduces the IF,shifts grain boundary peaks towards higher temperatures,and produces a small addi- tional peak at even higher temperature.The mechanism of GBIF is explained as the movement of defects of atomic size,namely point defects,at gram boundaries and/or their clusters un- der stress.