摘要
The interaction of oxide film with molten flux during aluminum brazing has been studied by means of X-ray powder diffraction. The following conclusions have been deduced: The swell- ing of aluminum oxide film is caused by Li^+ inserting into the vacancies of octahedral or tetrahedral structure of 0 atom skeleton in у-Al_2O_3 . The strength of oxide film decreases as the crytallinity increases by the treating of flux containing LiF.
The interaction of oxide film with molten flux during aluminum brazing has been studied by means of X-ray powder diffraction. The following conclusions have been deduced: The swell- ing of aluminum oxide film is caused by Li^+ inserting into the vacancies of octahedral or tetrahedral structure of 0 atom skeleton in у-Al_2O_3 . The strength of oxide film decreases as the crytallinity increases by the treating of flux containing LiF.