摘要
采用过氧乙酸对山羊绒进行正交氧化处理实验,分析过氧乙酸用量、时间、温度、助剂等因素处理后对纤维强力、毡缩球直径的影响程度。实验得到:对山羊绒纤维强力损伤的影响程度由大到小依次为:时间、温度、焦磷酸钠用量、过氧乙酸用量;对山羊绒纤维毡缩球直径的影响程度由大到小依次为:温度、过氧乙酸用量、焦磷酸钠用量、时间。
In this paper, peracetic acid was used for cashmere shrink-proofing treatment. The effect of peracetic acid content, treatment time, treatment temperature, and additives agent on the strength and the felt diameter of treated cashmere fibers was investigated. Experimental results showed that treatment time had a serious effect on fiber strength, then in turn were treatment temperature, additives agent, peraeetic acid. And treatment temperature had a serious effect on feh diameter, then in turn were peracetic acid, additives agent, treatment time.