冶金因素对钢点蚀诱发敏感性的影响 被引量:3

EFFECT OF METALLURGY FACTORS ON SUSCEPTIBILITY TO PITTING INITIATION IN STEELS
下载PDF
导出
摘要 选取有代表性冶金元素的几种低碳钢和低合金钢,通过在3%NaCl(pH=10)溶液中的极化实验比较它们之间的点蚀诱发敏感性,用电子探针(EPMA)分析钢中夹杂物诱发点蚀的腐蚀特征。结果表明,脱氧程度较差的沸腾钢的抗点蚀诱发能力明显优于脱氧程度完全的镇静钢,经过稀土处理的镇静钢的抗点蚀诱发能力有所改善,介于两者之间。镍铬系低合金钢的抗点蚀诱发能力优于锰系低合金钢,说明钢中合金元素对点蚀诱发敏感性有重要影响。钢中夹杂物是最主要的点蚀诱发源,夹杂物边界钢基体表面的氧化膜最薄弱,夹杂物诱发点蚀的最初腐蚀均始于该基体处。 Several low-carbon steels and low-alloy steels with representative metallurgical factors were selected. Their susceptibility to pitting initiation was compared by means of polarization test in 3% NaCl solution with pH=10. Characteristic of pitting initiated by inclusions in steels was analyzed with the EPMA. The results showed that the resistance of susceptibility to pitting in boiling steel was obviously better than that of killed steel, the resistance of susceptibility to pitting in killed steel treated by rare earth was improved, between boiling and killed steel. The resistance of susceptibility of Ni-Cr steel to pit was higher than that of Mn steel, which indicated the susceptibility to pitting initiation was significantly affected by alloy elements. The inclusions were the most primary sites of pitting initiation. Passivation film of boundary between steel matrix and inclusions was the weakest and pitting was firstly initiated there.
出处 《中国腐蚀与防护学报》 CAS CSCD 北大核心 2009年第2期127-131,共5页 Journal of Chinese Society For Corrosion and Protection
关键词 沸腾钢 镇静钢 低合金钢 点蚀 夹杂物 boiling steel, killed steel, low-alloy steel, pitting, inclusion
  • 相关文献

参考文献3

二级参考文献16

  • 1甘肃师范大学化学系编写组.简明化学手册[M].兰州:甘肃人民出版社,1980..
  • 2陈学群 孙小东 等.低碳钢中硫化物夹杂诱发点蚀的机理[J].海军工程学院学报,1997,(1):1-9.
  • 3陈学群,海军工程学院学报,1997年,1期,1页
  • 4甘肃师范大学化学系编写组,简明化学手册,1980年
  • 5苗中辉 陈学群 朱梅五.夹杂物对有机涂层下碳钢腐蚀初期过程的影响[J].海军工程学院学报,1998,10(4):23-30.
  • 6Sathler L, Muylder J V, Pourbaix M. Electrochemical behavior of iron in localized corrosion cells in the presence of chloride[A]. The Proceeding of the Seventh International Congress of Metallic Corrosion[C]. Canada:Toronto, 1978, 8:705~718
  • 7国家自然科学基金重大项目.材料海水腐蚀数据积累及腐蚀与防护研究试验总结报告[R].,1991..
  • 8Van Muylder. Comprehensive Treaties of Electrochemistry, Vol44,Electrochemical Materials Science [ M ]. OM Bockris J Ed, et al.New York:Plenum Press, 1981
  • 9Costa I, Faidi S E, Scantlebury J D. The effect of substrate minor compositional differences on the corrosion performance of coated steels[J]. Corros. SCi., 1993, 35(5 - 8): 1367~ 1374
  • 10林昌健,谢兆雄,田昭武.不锈钢点腐蚀发生的早期过程Ⅱ.电化学扫描隧道显微研究[J].腐蚀科学与防护技术,1997,9(4):259-264. 被引量:13

共引文献52

同被引文献27

引证文献3

二级引证文献12

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部